In Vivo Behavior of Injectable Fast-Setting Calcium Phosphate Cement

Li Min Dong,Wang Chen,Liu Rui,Jie Mo Tian,Zan Qingfeng
DOI: https://doi.org/10.4028/www.scientific.net/KEM.336-338.1625
2007-01-01
Key Engineering Materials
Abstract:The in vivo study was performed to evaluate the biocompatibility and osteogenous ability of injectable fast-setting calcium phosphate cement (CPC). Eighteen four-week-old New Zealand white rabbits were divided into six groups randomly, three in each group. According to the principle of self-contrast at the same time, cavities of 5mm in diameter and 6mm in depth were drilled in femoral condyle of rabbits. The materials were implanted into cavities of the left leg, the right leg as the blank control group, Rabbits were sacrificed at 2, 4, 8, 12, 16 and 24 weeks after surgery. The microstructure of specimens was observed using ESEM. The results showed that injectable fast-setting CPC had good fluidity and plasticity; it could be injected into bone defects and fast-set in situ. The start setting time was 5-8 min and the compressive strength was 25-30 MPa. The CPC had good biocompatibility and osteoconductivity, and benefited to the repair of bone defects.
What problem does this paper attempt to address?