Abstract:Sheet metals such as advanced high strength steels often exhibit varying degrees of anisotropy due to the existence of preferred orientation of their grain structures from the rolling process. While extensive research has been devoted to characterize and model anisotropic plasticity behavior over the past decades, only recently people began to tackle their anisotropic fracture behavior. The focus of these studies is almost always on the in-plane anisotropy, and ignores out of-plane fracture behavior. The reasons are two-folds: (1). Sheet metal deformation during a stamping or crash application is mostly thought as in a plane stress state and modeled as such, so there is no need to consider out-of-plane fracture behavior; and (2). It is very challenging to develop experimental techniques to reliably measure out-of-plane fracture strengths for sheet metals with a thickness only about 1 mm. In this paper, we theorize, based on strong empirical evidence, that the fracture strength of a thin sheet metal in out-of-plane shear is inherently weaker than that under in-plane shear, analogous to the interlaminar properties of composite laminates. This weakness is responsible for the so-called "shear fracture" behavior, often observed during the stamping operations of advanced high strength steels when the sheet metal flows around a tight radius. A new double-notched shear specimen with shear plane perpendicular to the thickness direction is carefully designed and tested to accurately measure the out-of plane shear fracture strength. Simulations are executed to validate the rationality of the out-of plane shear specimen design. Test results of a DP980 sheet show that the out-of-plane shear fracture strength is indeed about 15% lower than that measured under the in-plane shear condition. A new anisotropic ductile fracture model based on linear transformation of stresses is proposed to account for the out-of-plane fracture strength for AHSS sheets. The model is calibrated with experimental data, and the fracture surface is compared to the isotropic Mohr Coulomb (M-C) fracture model to illustrate its effectiveness.

Mesoscopic Criteria of Fracture for Advanced High-Strength Dual-Phase Steel Sheet

The Study and Application on Ductile Fracture Criterion of Dual Phase Steels During Forming

DAMAGE ACCUMULATION, FRACTURE AND POST FRACTURE ANALYSES FOR INITIALLY FLAWED STEEL STRUCTURES

Temperature Dependence of Meso Constitutive Parameters for Advanced High-Strength Steel

Fracture of dual phase steel sheets under uniaxial tension (I): experimental study with dic techniques

DUCTILE DAMAGE ANALYSIS FOR FRACTURE IN SHEET METAL FORMING BASED ON GTN MESOSCOPIC DAMAGE MODEL

Analysis and design of dual-phase steel microstructure for enhanced ductile fracture resistance

STUDY OF FAILURE CRITERION OF ADVANCED HIGH STRENGTH STEEL

Review on Fracture Criterion of Sheet Metal Forming

Fracture of dual phase sheets under uniaxial tension(Ⅱ):Nonlinear finite element analysis

Experimental and Numerical Fracture Characterization of DP1180 Steel in Combined Simple Shear and Uniaxial Tension

Anisotropic Fracture of Advanced High Strength Steel Sheets: Experiment and Theory

New Ductile Fracture Criterion for Prediction of Fracture Forming Limit Diagrams of Sheet Metals

Failure Mode And Ductility Of Dual Phase Steel With Edge Crack

Fracture Resistance of Advanced High-Strength Steel Sheets for Automotive Applications

Fracture prediction of high-strength steel sheet during in-plane compression-shear forming under negative stress triaxiality

A new shear and tension based ductile fracture criterion: Modeling and validation

Ductile Fracture Modelling of Steel Plates under Tensile and Shear Dominated States

Numerical Simulation and Experimental Verification of Ductile Fracture Criteria of Metals

Uniaxial Tension Simulation Using Real Microstructure-based Representative Volume Elements Model of Dual Phase Steel Plate

Experimental Study of Shear Fracture on Advanced High Strength Dual-Phase Steels