Abstract:In this study, Ti–Si–C composite coatings were synthesized via plasma spraying of agglomerated powders prepared by a spray drying/precursor pyrolysis technology using Ti, Si, and sucrose powders. The influence of Si content, ranging from 0 wt% to 24 wt%, on the microstructure, mechanical properties, and oxidation resistance of the composite coatings was investigated. Results show that the phase composition of the Ti–Si–C composite coatings changes with the increasing Si content. The coatings without Si addition consist of TiC and Ti3O; the coatings with 6–18 wt% Si are composed of TiC, Ti5Si3, and Ti3O; the coatings with Si content of 24 wt% form only TiC and Ti5Si3 phases. As the Si content increases, the hardness of the Ti–Si–C composite coatings increases first and then decreases, depending on the intrinsic hardness of the ceramic phases, the brittleness of Ti5Si3, and the defects such as pores and cracks. The Ti–Si–C composite coatings have high wear resistance due to the in-situ synthesized high-hardness TiC and Ti5Si3. Owing to the high brittleness of Ti5Si3, the increasing Si content leads to higher wear volume loss at room temperature, which can be partially improved in high-temperature wear tests. The oxidation resistance of Ti–Si–C composite coatings increases with the increase of Si content, and the higher the oxidation temperature, the more obvious the influence of the Si addition on oxidation resistance.

Deposition of SiO<sub>2</sub>/SiC Coating on Carbon Fiber to Enhance the Oxidation Resistance

Oxidation protection of carbon fibers by a reaction sintered nanostructured SiC coating

Microstructural and Tribological Properties of Cold Sprayed High Content Sicp/Al Coating by Sicp Mild-Oxidation Treatment

An AlPO4-SiC-MoSi2/SiC oxidation protective coating on carbon/carbon composites by pulse arc discharge deposition

Influence of SiC Coating on Antioxidation Property of Carbon Fibers

Effect of Al2O3 addition on the microstructure and oxidation behavior of SiC coating prepared by pack cementation on C/C composites

Influence Of Sic Coating On The Oxidation Behavior Of Pan Carbon Fiber At Elevated Temperatures

Oxidation behavior and cracking evolution of atmospheric plasma spraying Si and 60Si-40HfO2 bond coats at 1400 °C

Spraying Power Effect on Micro-Structure and Mechanical Property of TaSi2 Coating Prepared by Supersonic Air Plasma Spraying for SiC-Coated C/C Composites

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

Oxidation Resistance Of Carbon/Carbon Composites Coated With A Si-Mosi2 By Slurry Dipping Process

Oxidation Protection of C/C Composites with a Multilayer Coating of SiC and Si + SiC + SiC Nanowires

SiCn/SiC Oxidation Protective Coating for Carbon/carbon Composites

Oxidation protective AlPO4 coating for SiC coated carbon/carbon composites for application at 1773 K and 1873 K

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

Microstructure and Oxidation Resistant Property of C/C Composites Modified by SiC–MoSi2–CrSi2 Coating

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process

Effect of Si content on the microstructure and properties of Ti–Si–C composite coatings prepared by reactive plasma spraying

SiC Nanowire-Toughened SiC–MoSi2–CrSi2 Oxidation Protective Coating for Carbon/carbon Composites

Enhanced antioxidation and microwave absorbing properties of SiC/SiO2 coating on carbon fiber

Oxidation Behavior of Dense SiC Coating in Water Vapor and Its Mixed Atmosphere with Air

Deposition of SiO&lt;sub&gt;2&lt;/sub&gt;/SiC Coating on Carbon Fiber to Enhance the Oxidation Resistance