Abstract:Several series of Li1+/-yMn2O4+/-delta samples with the spinel structure were synthesized. These samples had different Li/Mn ratios (by varying the Li/Mn ratio used in stirling materials) and various oxygen contents (by controlling synthesis conditions, including temperature, heat-treatment time, and purging gas during both the solid-state reaction and annealing). In systematic studies of charge-discharge cycling behavior and in situ X-ray diffraction (XRD) at room temperature, it was found that both the charge/ discharge profile and the structural changes during cycling are closely related to the degree of oxygen deficiency created in the synthesis process. Their effects on the capacity fading are much more important than the Li/Mn ratio or other factors. A higher degree of oxygen deficiency is accompanied with a faster fading of capacity during cycling. In cells using spinel cathodes with an oxygen deficiency. the capacity fading during cycling occurs on both the 4.2 and 4.0 V plateaus. This behavior is quite different from that found in cathodes without an oxygen deficiency, where most of the capacity fading occurs on the 4.7 V plateau region only. Our in situ XRD results indicate clearly that the capacity fading on the 4.2 V plateau is related to the phase transition between the cubic II and cubic III (lambda -MnO2) structure, while the capacity fading on the 4.0 V plateau is related to the phase transition between the cubic I and cubic II spinel structures. The effects of oxygen deficiency on the structural phase transition of Li1+/-yMn2O4+/-delta-type materials at temperatures around 10 degreesC were also studied. It was found that this phase transition is closely related to the degree of oxygen deficiency of the material. In samples with no oxygen deficiency, this phase transition disappeared. (C) 2001 The Electrochemical Society.

Mechanism and Improvement for Capacity Fading of Spinel LiMn_2O_4

Improved Electrochemical Performance And Capacity Fading Mechanism Of Nano-Sized Limn0.9fe0.1po4 Cathode Modified By Polyacene Coating

Mechanism of Capacity Fading Caused by Mn (II) Deposition on Anodes for Spinel Lithium Manganese Oxide Cell

Mitigation of Cation Mixing of LiNiO2-based Cathode Materials by Li-doping for High-Performing Lithium-Ion Battery

Rate-dependent Electrochemical Reaction Mechanism of Spinel Metal Oxide Anode Studied by in Situ TEM

Mechanism of capacity fade of MCMB/Li1.1[Ni1/3Mn1/3Co1/3]0.9O2cell at elevated temperature and additives to improve its cycle life

Correlating Capacity Fading and Structural Changes in Li1 + y Mn2 − y O 4 − δ Spinel Cathode Materials: A Systematic Study on the Effects of Li/Mn Ratio and Oxygen Deficiency

Capacity Fading on Cycling of 4 V Li / LiMn2 O 4 Cells

Capacity Fade of Li[sub 1+x]mn[sub 2−x]o[sub 4]-Based Lithium-Ion Cells

Effectively Suppressing Dissolution of Manganese from LiMn2O4 Spinel Via a Novel Nanoscale Surface-Doping Approach

Surface Modification of Li1.03mn1.97o4 Spinels for Improved Capacity Retention

Capacity Fading on Cycling of 4 V Li∕LiMn[sub 2]O[sub 4] Cells

Specific Countermeasures to Intrinsic Capacity Decline Issues and Future Direction of LiMn 2 O 4 Cathode

MECHANISM ANALYSIS ON CAPACITY FADING OF SPINEL LITHIUM MANGANESE OXIDE CELL

Correlation Between Manganese Dissolution and Dynamic Phase Stability in Spinel-Based Lithium-Ion Battery

LiMn2O4 cathodes with F anion doping for superior performance of lithium-ion batteries

Surface Magnesium Substitution at Spinel Lithium Manganate 8a Tetrahedral Sites for Suppressed Manganese Dissolution and Enhanced Cycle Stability

Strengthening Reversibility at High Rate of Spinel LiMn2O4 by Aluminum and Copper Co-doping for Lithium Ion Battery

Capacity fading of high specific capacity spinel LixMn2-yTiyO4 as cathode material for Li-ion batteries

Strengthening Reversibility at High Rate of Spinel LiMn 2 O 4 by Aluminum and Copper Co-doping for Lithium Ion Battery

The Modification of Cathode Material LiMn2O4 for Lithium-Ion Batteries