Enhanced Electrochemical Performance of Li 1.3 Al 0.3 Ti 1.7 (PO 4 ) 3 Solid Electrolyte by Anion Doping

Jingrui Kang,Xu Guo,Rui Gu,Honglei Hao,Yi Tang,Jiahui Wang,Li Jin,Hongfei Li,Xiaoyong Wei
DOI: https://doi.org/10.1007/s12274-023-5890-9
IF: 9.9
2024-01-01
Nano Research
Abstract:Nowadays, the majority of the studies on the substitution are focused on cations (such as Y3+, Ti4+, P5+, etc.) in Li1.3Al0.3Ti1.7(PO4)3 (LATP), while there are few studies on the substitution of anion O2−. In this work, the modified LATP with a series of LiCl (LATPClx, x = 0.1, 0.2, 0.3, 0.4) additives is prepared to enhance ionic conductivity. The successful introduction of Cl− makes the length of the c axis decrease from 20.822(2) to 20.792(1) Å, and the bulk conductivity of 2.13 × 10−3 S·cm−1 is achieved in LATPCl0.3. Moreover, the Al/Ti-O1/Cl1 and Al/Ti-O2/Cl2 distance decrease, while the Li1-O2/Cl2 distance increases. Lithium ions migrate more easily in the nanochannel of M3-M1-M3. In addition, the LiCl additive increases the relative density and the grain boundary conductivity of LATPClx compounds. Naturally, a higher ionic conductivity of 2.12 × 10−4 S·cm−1 and a low activation energy of 0.30 eV are obtained in LATPCl0.3. Correspondingly, the symmetric cell exhibits a low overpotential of ±50 mV for over 200 h in LATPCl0.3. The solid-state Li∣LATPCl0.3∣NCM811 (NCM811 = LiNi0.8Co0.1Mn0.1O2) battery exhibits high initial capacity 185.1 mAh·g−1 with a capacity retention rate of 95.4
What problem does this paper attempt to address?