Abstract:The existence of impuritiy phases such as Bi25FeO39 and Bi2Fe4O9 has led to high leakage current in BiFeO3 multiferric materials, which consequently restricts further understanding of its coupling between magnetic and polarization orders. Prior to the attempts to synthesize pure-phase BiFeO3 ceramics, the phase transition involved in the reaction sintering should be clarified. In the present, the phase transformations during the reaction sintering process of BiFeO3 ceramics with different molar ratio of Bi2O3/Fe2O3 in air were studied via High Temperature X-ray Diffraction technique (HT-XRD), Rietveld refinement quantification, and High Temperature Raman Spectroscopy (HT-Raman). The thermal stabilities of BiFeO3, Bi25FeO39 and Bi2Fe4O9 ceramics were also studied by such methods. The qualitative phase distributions after heating were analyzed by Electron Backscattered Diffraction (EBSD). Results show that the phase transition from monoclinic to cubic for Bi2O3 was well done, which usually taken place at 700 °C. The Fe2O3 did 1036 无机材料学报第 34 卷 not react with Bi2O3 to form BiFeO3 until that transition finished. In addition, BiFeO3, Bi25FeO39 and Bi2Fe4O9 phases are not in thermodynamic stable state during the cooling process for Bi excess samples. Bi2O3 excess can effectively inhibit the formation of impurities and promote the sintering of BiFeO3 phase. The phase content of BiFeO3 mainly depends on the molar ratio of Bi2O3/Fe2O3, and 1.03 : 1 is optimum. Combining with our previous research results, it is found that the effective parameters for the synthesis of BiFeO3 strongly depend on the excessive Bi and rapid heating and cooling rate. This work may provide useful experimental guidance for the preparation of pure-phase BiFeO3 ceramics.

Co-precipitation/hydrothermal Synthesis of BiFeO 3 Powder

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Hydrothermal Synthesis, Photocatalytic and Magnetic Properties of Pure-Phase Bi2Fe4O9 Microstructures

Synthesis, Structures and Properties of Single Phase BiFeO 3 and Bi 2 Fe 4 O 9 Powders by Hydrothermal Method

Controllable Synthesis of (nh4)fe2(po4)2(oh)·2h2o Using Two-Step Route: Ultrasonic-intensified Impinging Stream Pre-Treatment Followed by Hydrothermal Treatment.

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Effect of poly sodium-p-styrenesulfonate on the phase formation and morphology of the hydrothermally synthesized bismuth ferrite powders

Structure and phase transition of BiFeO 3 cubic micro-particles prepared by hydrothermal method

Synthesis and Magnetic Property of Submicron Bi2fe4o9

Low-temperature Synthesis of Bi4Ti3O12 Nanocrystals by Hydrothermal Method

Bi4Ti3O12 nanocrystals synthesized via hydrothermal reaction

Bismuth–iron-based precursor: preparation, phase composition, and two methods of thermal treatment

Stoichiometric Ratio on Phase Transformation in Reaction Sintering of BiFeO3 Ceramics Study: a High Temperature X-ray Diffraction Study

A facile two-step hydrothermal route for the synthesis of γ-Fe 2 O 3 nanocrystals and their magnetic properties

Phase and Morphology Evolution of Bismuth Ferrites Via Hydrothermal Reaction Route

Chemical Co-Precipitation Synthesis and Properties of Pure-Phase BiFeO3

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Mineralizer-Assisted Hydrothermal Synthesis and Characterization of BiFeO<sub>3</sub> Nanoparticles

Preparation of BiFeO3 Thin Films by Chemical Solute Method

Low-temperature synthesis of Bi2Fe4O9 nanoparticles via a hydrothermal method