Effect of Ni Interlayer Thickness on the Welding Morphology and Mechanical Properties of SPS Diffusion-Welded YG8/40Cr Joints

Yafei Pan,Xiaolong Yang,Zhenyao Fan,Dawei Liu,Jiuxing Zhang,Siyao Xie,Yong Du,Fenghua Luo,Lei Huang
DOI: https://doi.org/10.1007/s11665-023-08480-6
IF: 2.3
2023-01-01
Journal of Materials Engineering and Performance
Abstract:Diffusion welding of YG8 and 40Cr was carried out by spark plasma sintering. The influence of Ni interlayer with different thicknesses varying from 0 to 500 μm on the welding morphology and mechanical properties of joints was studied. The fracture position moved from the cemented carbide substrate toward the connection interface with the increase in the thickness of the Ni intermediate layer. The joint with nickel-free interlayer and 100-μm thick fractured during electrical discharge machining due to the large residual stress. The bending strength of the joints enhanced with the increase in the Ni intermediate layer from 200 to 300 μm, and a maximum flexural strength of 982 MPa was obtained with the thickness of the Ni intermediate layer to be 300 μm, which was up to 97
What problem does this paper attempt to address?