Abstract:Limited by flammability, wood and wood-based materials face challenges in distinguishing themselves as structural materials or finishing materials. Once burning, they can produce toxic gases detrimental to humans and the environment. Therefore, it is critical to make clear whether fire-retardant wood construction materials are insusceptible to fire and not the sources of toxic gases. This study aimed to evaluate flame-retardant plywood from the aspects of flammability and the toxic gas and smoke generation during combustion. The flame-retardant plywood was manufactured by impregnating a flame-retardant resin in line with International Maritime Organization (IMO) standards. The research results indicate that seven out of the eight kinds of toxic gases listed by the IMO, other than CO, were not detected during the combustion of the flame-retardant plywood. While CO was detected, its quantities under three test conditions are below the corresponding thresholds. Therefore, unlike synthetic resin products, flame-retardant plywood is a promising finishing material that can reduce the damage from toxic gases in the event of a fire. In the smoke generation tests, the mass reduction rate of flame-retardant plywood increased from 13% to 18% and then to 20% as the test condition became more severe. Under the same circumstances, the average maximum specific optical density also followed an upward trend, whose values (75.70, 81.00, and 191.20), however, still met the IMO standard of below 200. This reflects that the flame-retardant plywood is competent as a finishing material. Further, flammability was evaluated, and the critical flux at extinguishment (CFE), total heat release (Qt), and peak heat release rate (Qp) were determined to be 49.5 kW/m2, 0.21 MJ, and 0.66 kW, respectively, which all did not reach the corresponding thresholds given by the IMO. To sum up, flame-retardant plywood has satisfactory flame-retardant performance and meets fire safety standards, showing the potential to be an attractive finishing material for building and construction.

Indoor functional plywood with electrothermal response, flame retardancy, and moisture-proof performance and enhanced surface temperature with nano-SiO2 film

Sandwich-structure inspired super-tough and fire-resistant plywood containing vinyl acetate-ethylene based adhesive reinforced by melamine amino trimethyl phosphate and sodium lignosulfonate

A Strong, Tough and Fire-Retardant Biomimetic Multifunctional Wooden Laminate

Preparation of Organic-Inorganic Phosphorus-Nitrogen-Based Flame Retardants and Their Application to Plywood

Reversible Photo-, Thermal-, and Ph-Responsive Functionalized Wood with Fluorescence Emission.

A strong, flame-retardant, and thermally insulating wood laminate

An environment-friendly, fire-resistant, thermal-insulating and mechanical-robust wood with anisotropic capacitive pressure-sensitive performance

Fire-retardant anti-microbial robust wood nanocomposite capable of fire-warning by graded-penetration impregnation

Preparation and Properties of Flame Retardant and Antistatic Foamed Wood–Plastic Composite with APP/ZB System

Performance Evaluation of Carbon Fiber Fabric-Reinforced Formaldehyde-Free High-Strength Plywood

Improvement in Monterey pine of the flame retardancy, thermal conductivity, and mechanical performance through incorporating functional epoxy resin

Construction of a continuous flame-retardant network made from wood in epoxy resin

Towards high performance wood composites through interface customization with cellulose-based adhesive

Dual-functional intumescent fire-retardant/self-healing water-based plywood coatings

Flame-retardant wood-based composite phase change materials based on PDMS/expanded graphite coating for efficient solar-to-thermal energy storage

Toxic Gas and Smoke Generation and Flammability of Flame-Retardant Plywood

Effective strategy for fabricating surface impregnated and unilaterally densified wood with furfuryl alcohol/flame retardants for enhanced mechanical performance and flame retardancy

Robust, Fire-Retardant, and Water-Resistant Wood/Polyimide Composite Aerogels with a Hierarchical Pore Structure for Thermal Insulation

Multifunctional Flame-Retardant, Thermal Insulation, and Antimicrobial Wood-Based Composites.

Combustion Behavior and Thermal Degradation Properties of Wood Impregnated with Intumescent Biomass Flame Retardants: Phytic Acid, Hydrolyzed Collagen, and Glycerol

Nanosheet-coated synthetic wood with enhanced flame-retardancy by vacuum-assisted sonocoating technique