Preparation of Composite Nanoparticles of Fe-Zn Bioxide Using Surface Modification and Their Subsequent Characterization
Longlong Chen,Jian Li,Yueqiang Lin,Xiaodong Liu,Lihua Lin,Decai Li
DOI: https://doi.org/10.1109/tmag.2014.2305133
IF: 1.848
2014-01-01
IEEE Transactions on Magnetics
Abstract:During the liquid-phase synthesis of gamma-Fe2O3 nanoparticles using a chemically induced transition in FeCl2 solution (400 mL, 0.25 M), the surface modification of the particles was undertaken by adding ZnCl2 solution, in an attempt to prepare composite nanoparticles. The magnetization, morphology, chemical composition, and crystal structure of the product were characterized using a vibrating sample magnetometer, transmission electron microscopy, X-ray diffraction, energy-dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The experimental results showed that when the concentration of ZnCl2 solution did not exceed 2 M (50 mL), the gamma-Fe2O3-ZnFe2O4 bioxide composite nanoparticles coated by FeCl3 center dot 6H(2)O could be prepared. These particles were nearly spherical and their average size was about 11 nm; specific saturation magnetization was about 48 Am-2/kg. The molar, mass, and volume percentages of every composition phase, as well as the average density of the composite nanoparticles, were estimated from the characterization results. A particle model with a core that is gamma-Fe2O3 covered with ZnFe2O4 is proposed.