Abstract:Cr doped diamond-like carbon (DLC) coating was deposited on the carburized Ti6Al4V alloy (TA) by magnetron sputtering (MS). The physical and chemical characteristics of Cr doped DLC coating were obtained using scanning electron microscope, energy dispersive spectroscope, Raman spectrometer, X-ray photoelectron spectroscopy and Fourier transform infrared, and the mechanical property and adhesion force were analyzed by nanoindenter and scratch tester. The effects of carburizing treatment on the coefficient of friction (COF) and wear mechanism of Cr doped DLC coatings were investigated on a ball-on-disk tribometer. The results show that the adhesion force and mechanical property of Cr doped DLC coating deposited on the carburized TA are higher than those deposited on the original TA. The average coefficients of friction (COFs) of Cr doped DLC coatings deposited on the original and carburized TAs under the dry-friction condition are 0.157 and 0.143, respectively, showing that the carburizing treatment has the obvious effect of friction reduction for the Cr doped DLC coating. The wear mechanism of Cr doped DLC coating deposited on the carburized TA is combined action of abrasive wear and adhesive wear, which are contributed to the enhancement of mechanical property of Cr doped DLC coating by carburization treatment. Furthermore, the average COFs of Cr doped DLC coatings deposited on the original and carburized TAs under the oil-lubrication condition are 0.152 and 0.131, respectively, which are superior to those under the dry-fiction condition. The carburizing treatment promotes the formation of self-repairing carbonyl of Cr doped DLC coating, and the oil-wet characteristic of Cr doped DLC coating with the aromatic aldehyde of CO as the functional group plays the main role of friction reduction.

Tribological Properties of DLC Coatings with Varying Cr Concentration in Water Lubrication

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

Microstructure, Mechanical, and Tribological Properties of Cr-Ti-Si-N Coatings

Tribological Properties of Cr(Si)CN Coatings Sliding Against Different Mating Balls in Water

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

Tribological Behavior of Diamond Like Carbon Film Sliding Against Cocrmo or Al2o3 in Air and Water Environment

Tribological and electrochemical properties of Cr–Si–C–N coatings in artificial seawater

Microstructure, mechanical properties and high-speed dry-cutting performance of AlCrSiCN composite coatings

Influence of Trimethylsilane Flow on the Microstructure, Mechanical and Tribological Properties of CrSiCN Coatings in Water Lubrication

Effect of carburizing treatment on microstructural, mechanical and tribological performances of Cr doped DLC coating deposited on Ti6Al4V alloy

Influence of Cr on the Surface Properties of the Micro-Textured WC+Co Alloy Coating

Microstructure and Tribological Properties of Multilayered ZrCrW(C)N Coatings Fabricated by Cathodic Vacuum-Arc Deposition

Structure and Tribological Properties of CrTiAlCN Coatings with Various Carbon Contents

The development of B/Cr co-doped DLC coating by FCVA deposition system and its tribological properties at 300 °C

Influence of C Content on the Structure, Mechanical and Tribological Properties of CrAlCN Films in Air and Water-Based Cutting Fluid

Role of carbide content in governing the mechanical and tribological properties of DLC/Cr 3 C 2 –NiCr duplex coatings

Tribological and dry drilling performance of WS2/Cr-AlCrN coatings

Influence of Ag target current on the structure and tribological properties of CrMoSiCN/Ag coatings in air and water

Achieving superlubricity and high adhesion strength of hydrogenated amorphous carbon film with Al/Cr/Si-doping

Tribological performance of DLC-coated ceramics against cemented carbide under dry sliding conditions

Comparative study on microstructure, bio-tribological behavior and cytocompatibility of Cr-doped amorphous carbon films for Co-Cr-Mo artificial lumbar disc