Oxidation Behaviours of Ir-Hf and Ir-Zr Coatings under Different Air Pressures at 1800℃

Fayuan Li,Li'an Zhu,Kaili Zhang,Zhen Wang,Yicong Ye,Shun Li,Yu Tang,Shuxin Bai

DOI: https://doi.org/10.1016/j.surfcoat.2023.129640

2023-01-01

Abstract:In order to improve the oxidation resistance of Ir, multilayer Ir-Hf and Ir-Zr coatings with gradually increasing content of alloying elements from inside out were formed in situ on Ir by pack cementation. The oxidation behaviors and microstructural evolution of the Ir-Hf and Ir-Zr coatings oxidized under different air pressures at 1800 degrees C for 1 h were explored and the oxidation mechanisms were revealed. The results showed that the oxidation resistances of the Ir-Hf and Ir-Zr coatings at 1800 degrees C were much better than that of pure Ir and increased with the decrease of pressure. At 101 kPa, the mass loss rates of the Ir-Hf and Ir-Zr coatings were 0.52 x 10-3 and 0.48 x 10-3 mg center dot cm- 2 center dot s- 1, respectively. The as-oxidized Ir-Hf and Ir-Zr coatings mostly exhibited morphologies of internal oxidation with a quasi-gradient transition structure and both coatings were prone to external oxidation with decreasing pressure. The critical pressure for the internal to external oxidation transition of the Ir-Zr coatings was-1 kPa and higher than that of the Ir-Hf coatings.