Abstract:The augmented finite element method (A-FEM) is used to study the fundamental composite failure problem of delamination and associated damage events spreading from a stress concentrator during tensile loading. The solution exploits the ability of A-FEM to account for coupled multiple crack types that are not predetermined in shape or number. The nonlinear processes of each fracture mode are represented by a cohesive model, which provides a unified description of crack initiation and propagation and can also describe crack coalescence and bifurcation. The study problem is an orthogonal double-notched tension specimen, in which delaminations interact with transverse ply cracks, intra-ply splitting cracks, non-localized fine-scale matrix shear deformation, and fiber breaks. Cohesive laws and constitutive laws for matrix shear deformation are calibrated using literature data from independent tests. The calibrated simulations are mesh independent and correctly reproduce all qualitative aspects of the coupled damage evolution processes. They also correctly predict delamination sizes and shapes, the density of transverse ply cracks, the growth rate of splitting cracks, softening of the global stress–strain curve, and the ultimate strength. A sensitivity analysis relates variability in cohesive law parameters to predicted deviance in engineering properties. Given the known variability in cohesive law parameters, the predicted deviance in ultimate strength agrees with that in experimental data. The importance of including the interactions between different crack systems and non-localized shear deformation is demonstrated by suppressing the presence of separate mechanisms; the predicted delamination shapes, splitting crack growth rate, and the stress–displacement relationship fall into significant error.

Numerical Simulation of Compact-Tension Specimens Repaired by CFRP

Fatigue behavior and digital image correlation monitoring of steel plates with mixed-mode edge cracks repaired with CFRP materials

Finite Element Analysis for the Fatigue Behavior of Steel Plates Strengthened with CFRP Plates

Debonding development in cracked steel plates strengthened by CFRP laminates under fatigue loading: Experimental and boundary element method analysis

Experimental Study on Interfacial Bond Behavior between CFRP Sheets and Steel Plates under Fatigue Loading

Cracking Behavior of Cfrp Laminate-Strengthened Rc Beams with Premechanical and Postmechanical Environmental Damage

STUDY ON FATIGUE BEHAVIOR OF CRACKED TENSILE STEEL PLATES REINFORCED WITH CFRP PLATES

Behavioral Simulation Model for Sfrc and Application to Flexural Fatigue in Tension

Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

Rigorous SIF-based prediction of fatigue life improvement for prestressed-CFRP-repaired cracked steel plates

An experimental study on fatigue debonding growth of RC beams strengthened with prestressed CFRP plates

PARAMETER STUDY ON STEEL PLATES REINFORCED BY CFRP PLATES WITH FINITE ELEMENT METHOD

Crack Propagation and Debonding Development of CFRP Laminate Strengthened High-Strength Steel Plates under Fatigue Loadings

Numerical simulation of distortion-induced fatigue crack growth using extended finite element method

Experimental and 3D Numerical Study on CFRP–Concrete Interface Under Dynamic Loading

Fatigue Behavior of Cracked High-Strength Steel Plates Strengthened by CFRP Sheets

Prediction of Bending Fatigue Life of Cracked Out-of-Plane Gusset Joint Repaired by CFRP Plates

Structural Fatigue Crack Propagation Simulation and Life Prediction Based on Improved XFEM-VCCT

An investigation of Fatigue Behavior and Residual Strength Model of Steel-GFRP Composite Bar

Finite element simulation of debonding in FRP-to-concrete bonded joints

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension