Significantly improved strength of the TiC/TA19 composites via interface and dislocation strengthening
Zekun Zheng,Zhaohui Zhang,Xiang Li,Xuezhe Zhang,Guodong Sun,Linbo Li,Yongqing Fu,Ahmed Elmarakbi,Longlong Dong
DOI: https://doi.org/10.1016/j.carbon.2024.119581
IF: 10.9
2024-09-14
Carbon
Abstract:For titanium matrix composites (TMCs) with a dual-phase structure, yield strength (YS) is typically governed by the hard α phase rather than the soft β phase in the matrix alloy. Therefore, by controlling the precipitation of nanoscale secondary α phases (α s ) within the β phase, lattice distortion can be induced, leading to dislocation pile-ups at the α s /β phase interface, thereby achieving strengthening of the matrix interface. Herein, TiC/TA19 composites were fabricated using spark plasma sintering, and induced the dispersion and pinning of nanoscale α s phases from the β phase at the α s /β phase interface through multi-pass cumulative rolling, achieving super high strength. In particular, the nanoscale α s phase exhibits two typical Burgers orientation relationships with the β phase, i.e. (0001) α s//(110) β & [11 2− 0] α s//[ 1− 11] β and (0001) α s//(01 1− ) β & [11 2− 0] α s//[ 1− 11] β , respectively. Compared with the yield strength of sintered composites, when the rolling reduction was 75 %, the YS of TiC/TA19 composites increased by 33.7 %, reaching 1368 MPa, and the elongation was 3.6 %, only 0.7 % lower than that of sintered composites (4.3 %). The enhanced strength is mainly attributed to the α s precipitation for α s /β interface strengthening and dislocation strengthening derived from the TiC and nanoscale α s precipitates. The volume fraction of dynamic recrystallization grains in TiC/TA19 composites increased with the rolling reduction, and more pyramidal slip systems were activated to coordinate the plastic deformation of the composites. This study offers a promising route to fabricating superior high-strength TMCs and provides new insights into balancing strength and ductility.
materials science, multidisciplinary,chemistry, physical