Abstract:In this study, CoMn2O4 and Cu0.5Co0.5Mn2O4 spinels are examined as protective coatings for chromium diffusion in metallic interconnect of solid oxide fuel cell. Both spinels are prepared by co-precipitation technique in order to obtain high temperature conducting spinels. The spinels obtained after 4 h of calcinations in air at 500 °C exhibit tetragonal crystal structure with average grain size between 90 and 100 nm. Cu0.5Co0.5Mn2O4 spinel exhibits superior electrical conductivity over CoMn2O4 and both display NTCR (negative temperature co-efficient of resistance) behavior illustrating their use as a protective layer on interconnects for fuel cells operating at higher temperatures. Doctor-blade employed spinel coating over SUS430 alloy exhibits good adhesion between protective spinel layer and metallic alloy. Cross section micrographs reveal presence of nanosized and highly dense grains capable to resist the outflow of chromium ions present in SUS430. Mass gain and diffusion rate constant (Kp) was high for CoMn2O4 coated SUS430 illustrating Cu0.5Co0.5Mn2O4 spinel as a better protective coating layer for interconnect application. Chromium outflow is restricted and the same is evident from all cross-section micrographs of spinel coated SUS430 specimens subjected for oxidation up to 1000 h. Estimated thickness of Cr2O3 layer was ∼15 nm for CoMn2O4 whereas Cu0.5Co0.5Mn2O4 coated SUS430 specimen had ∼12.5 μm thickness at the SUS430/spinel interface demonstrating superior resistance to chromium outflow. The area specific resistance was lowest for Cu0.5Co0.5Mn2O4 coated specimen (between 14 mΩcm2 – 15 mΩcm2) followed by CoMn2O4 coated specimen reiterating Cu0.5Co0.5Mn2O4 as efficient protective coating material for SUS430 SOFC interconnect.

In-situ formed CuFe2O4 spinel coating by electroplating method for solid oxide fuel cell interconnect

Cu-Fe spinel coating as oxidation barrier for Fe-16Cr metallic interconnect in solid oxide fuel cells

Cufe2o4 Nano-Spherical Powder Directly Served As Interconnect Coating for Solid Oxide Fuel Cells Applications

Investigation of MnCu0.5Co1.5O4 spinel coated SUS430 interconnect alloy for preventing chromium vaporization in intermediate temperature solid oxide fuel cell

Mn 1.4 Co 1.4 Cu 0.2 O 4 spinel protective coating on ferritic stainless steels for solid oxide fuel cell interconnect applications

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Cyclic oxidation of Mn–Co spinel coated SUS 430 alloy in the cathodic atmosphere of solid oxide fuel cells

Oxidation behavior of Cu-doped MnCo 2 O 4 spinel coating on ferritic stainless steels for solid oxide fuel cell interconnects

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

A Promising NiCo2O4 Protective Coating for Metallic Interconnects of Solid Oxide Fuel Cells

Oxidation of MnCu0.5Co1.5O4 Spinel Coated SUS430 Alloy Interconnect in Anode and Cathode Atmospheres for Intermediate Temperature Solid Oxide Fuel Cell

Application of sol–gel technique to synthesis of copper–cobalt spinel on the ferritic stainless steel used for solid oxide fuel cell interconnects

Protective coatings for Cr2O3-forming interconnects of solid oxide fuel cells

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

CoMn2O4 and Cu0.5Co0.5Mn2O4 spinels as efficient protective coating layers on SUS430 for SOFC interconnect

Metallic Co with Reactive Element Oxide Composite Coatings for Solid Oxide Fuel Cell Interconnect Applications

NiMn2O4 Spinel As an Alternative Coating Material for Metallic Interconnects of Intermediate Temperature Solid Oxide Fuel Cells

Cu and Y doped (Co, Mn)3O4 spinel coatings on Crofer ferritic alloy by composite electrodeposition

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects