A New Benzotriazole Phosphite Ammonium Salt Derivative (PN) Extreme Pressure Additive to Improve Gear Oil Tribological Properties

Fengqi Fan,Qi Liu,Kang Zhou,Liping Wang,Binbin Wei,Guangneng Dong

DOI: https://doi.org/10.21203/rs.3.rs-291405/v1

2021-01-01

Abstract:Abstract In this paper, a new benzotriazole phosphite ammonium salt derivative extreme pressure additive called PN was synthesized. Four-ball experiments and SRV experiments were used to test the high temperature and extreme pressure performance of PN additive, and comparisons were made with the commonly used additives including ZDDP and T304. The results show that the COF and wear amount of the PN additive in the four-ball experiment were much smaller than that of the ZDDP and T304 additives. The COF of the PN additive in the RSV experiment changed slightly with temperature, and it had better high temperature extreme pressure performance in friction reduction than the traditional ZDDP and T304 additives. When the temperature was 120oC, the COF of PN was about 30% lower than that of traditional additives. Thermogravimetric analysis showed that the failure temperature of PN additives was within 180-200oC, and the thermal stability was better than that of ZDDP and T304. After the four-ball test, SEM was used to observe the morphology of wear spots on the ball surface. It was found that the wear spots containing PN additive had slight adhesive wear, while those containing ZDDP and T304 showed serious adhesion and ploughing wear, and the surface appeared peeling and tearing. XPS was used to detect the chemical composition of friction surface containing PN additive, and thus the formation process of film on frictional surface was analyzed.