Abstract:For microelectronic industry, Cu-based substrate and epoxy molding compound (EMC) interface is inherently weak and most likely to delaminate, well-known as a major threat for integrated circuits (ICs) reliability. In this paper, hierarchical whisker-like oxide/Cu cone structure was for the first time to be fabricated by combining electroless plating with heat treatment methods to enhance the interface adhesion between Cu-based substrate and EMC. The surface morphology was characterized by scanning electron microscope (SEM). Result shows that the hierarchical whisker-like oxide/Cu cone film is fine, dense and uniform; Single Cu cone structure is about 3-5 μm in height and 1 μm in root diameter; a layer of whisker-like oxide grows perpendicularly to circular surface of Cu cone, with length ranging from tens to hundreds of nanometers. Adhesion strength between the as-prepared substrates and EMC were measured by button shear test. With consideration of oxidation caused by practical processes (e.g. wire bonding), the interface of EMC and porous oxide formed at 260°C for 5 min was taken as standard sample, representative of practical interface. To further study the effect of whisker-like oxide and Cu cone solely on adhesion performance, whisker-like oxide, porous oxide/Cu cone were investigated as well. Button shear test results reveal that interfacial adhesion strength of EMC and whisker-like oxide, porous oxide/Cu cone, hierarchical whisker-like oxide/Cu cone are 85%, 110% and 162% higher than that of standard interface. Moreover, the mechanism for adhesion improvement was discussed by facture surface observation, failure path assumption and force-displacement curve analysis. Results show that interface of EMC and hierarchical whisker-like oxide/Cu cone exhibits brittle/ductile property with about 3-5 μm thick EMC left on the fracture surface, indicating cohesive failure caused by remarkable mechanical interlocking effect. © 2011 Elsevier Ltd. All rights reserved.

Grain-boundary/interface Structures and Scatterings of Ruthenium and Molybdenum Metallization for Low-Resistance Interconnects

Adhesion improvement of Cu-based substrate and epoxy molding compound interface by hierarchical structure preparation

Surface Sulfurization of Liner and Ruthenium Metallization to Reduce Interface Scattering for Low-Resistance Interconnect

RuAl intermetallic compound of low resistivity scaling and high thermal stability as potential interconnect metallization

Utilizing H2S to Sulfurize Transition Metal and Oxide Barriers for Suppressing Resistivity Scaling of Ruthenium Metallization

Modification and Characterization of Interfacial Bonding for Thermal Management of Ruthenium Interconnects in Next-Generation Very-Large-Scale Integration Circuits

Functionalizing Self-Assembled Monolayers to Reduce Interface Scattering in Ruthenium/dielectric for Next-Generation Microelectronic Interconnects

First principles evaluation of fcc ruthenium for use in advanced interconnects

Numerical evaluation of grain boundary electron scattering in molybdenum thin films: A critical analysis for advanced interconnects

Interdiffusion reliability and resistivity scaling of intermetallic compounds as advanced interconnect materials

Mechanisms of Scaling Effect for Emerging Nanoscale Interconnect Materials

Effect of ionic strength on ruthenium CMP in H 2 O 2 -based slurries

Epitaxial metals for interconnects beyond Cu

Studying the applicability of amorphous metal alloys as interface material for power electronics packaging

(Digital Presentation) On Epitaxial Electrodeposition of Co, Ru and Cu for Interconnect Applications

Confined Magnetization at the Sublattice-Matched Ruthenium Oxide Heterointerface

Studies of two-dimensional MoS2 on enhancing the electrical performance of ultrathin copper films

Three-dimensional atomic interface between metal and oxide in Zr-ZrO2 nanoparticles

The Inhibition of Enhanced Cu Oxidation on Ruthenium∕Diffusion Barrier Layers for Cu Interconnects by Carbon Alloying into Ru

Ultrathin, sputter-deposited, amorphous alloy films of ruthenium and molybdenum

Investigation of Interface Interactions Between Monolayer MoS 2 and Metals: Implications on Strain and Surface Roughness