Abstract:In this paper ,the precursor of Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4/PVP and Co0 .6 Ni0 .3 Zn0 .1 Fe2 O4/PVP nanofibers with uniform diameter and smooth surface were prepared by electrospinning technique .Then the Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4/PVP and Co0 .6 Ni0 .3 Zn0 .1-Fe2 O4/PVP nanofibers were obtained via heat treatment at 500—900 ℃ .The phase ,morphology ,structure and magnetic properties of the resultant Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4 and Co0 .6 Ni0 .3 Zn0 .1 Fe2 O4 nanofibers were characterized by TG-DSC ,XRD ,SEM and VSM respectively .The results show that the pure phase and well crystallized Co0.6Ni0.3Cu0.1Fe2O4 and Co0.6Ni0.3Zn0.1Fe2O4nanofibers or staple fibers can be obtained after heat treatment in the air by heat treatment at 500—900 ℃ .When the temperature is at 700 ℃ ,the diameter of Co0.6 Ni0.3 Cu0.1 Fe2O4 and Co0.6 Ni0.3 Zn0.1 Fe2O4 nanofibers with smooth surface is about 80 nm ,and moreover ,the Co0.6Ni0.3Cu0.1Fe2O4 nanofibers retain a high remanence ratio (Mr/Ms) and a coercivity of 0 .56 and 1088 .87 Oe respectively .At 500 ℃ ,600 ℃ ,700 ℃ ,800 ℃ ,900 ℃ ,Co0 .6 Ni0 .3 Zn0 .1 Fe2 O4 nanofibers exhibit the intensities of saturation magnetization which are 14 .5% ,7% ,16% ,10 .7% ,8% higher than those of Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4 nanofibers respectively ,as well as the coercive forces which are 38% ,51% ,50% ,46% ,46 .7% lower than Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4 nanofibers respectively .The differences of saturation magnetization and coercivity of the two nanofibers provide a good reference for electromagnetic applications of CoNi ferrite .

Facile electrospinning preparation of tunable flexible magnetism nanofiber

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Electrospinning Of Fe, Co, And Ni Nanofibers: Synthesis, Assembly, And Magnetic Properties

Flexible Coaxial Nanofibers: A Strategy to Realize Tunable and Enhanced Magnetic‐Luminescent Bifunctionality

Preparation of Fe3O4/PVP magnetic nanofibers via in situ method with electrospinning

Single Flexible Nanofiber to Simultaneously Realize Electricity-Magnetism Bifunctionality

Fabrication of Fe3O4/PVA Nanofibers by Electrospinning with a Magnetic Field

A New Strategy to Assemble Enhanced Magnetic–photoluminescent Bifunction into a Flexible Nanofiber

Fabrication and characterization of FePt magnetic nanofibers via electrospinning technique

One-pot Coaxial Electrospinning Fabrication and Properties of Magnetic-Luminescent Bifunctional Flexible Hollow Nanofibers

Fabrication of Magnetic Nanofibers by Needleless Electrospinning from a Self-Assembling Polymer Ferrofluid Cone Array

Tuned magnetism–luminescence bifunctionality simultaneously assembled into flexible Janus nanofiber

Electrospinning fabrication of flexible Fe3O4 fibers by sol-gel method with high saturation magnetization for heavy metal adsorption

Fabrication and Magnetic Properties of Electrospun Cobalt Nanofibers

Tunable and enhanced simultaneous magnetism-luminescence bifunctionality assembled into a coaxial nanofiber

1D Magnetic Materials of Fe 3 O 4 and Fe with High Performance of Microwave Absorption Fabricated by Electrospinning Method

Effect of Fe3O4 nanoparticles on magnetic electrospun nanofibers

Electrospinning Fabrication of High-Performance Magnetic@photoluminescent Bifunctional Coaxial Nanocables

Robust SiO2-modified CoFe2O4 hollow nanofibers with flexible room temperature magnetic performance.

Fabrication of Magnetic-Luminescent Bifunctional Composite Nanofibers Via Facile Electrospinning

Structure and Magnetic Properties of Electrospun Co0.6Ni0.3Zn0.1Fe2O4 and Co0.6Ni0.3Cu0.1Fe2O4 Nanofibers