Improving bond strength of translucent zirconia through surface treatment with SiO 2 –ZrO 2 coating

Tiehan Cui,Qiao Du,Guangliang Niu,Jiaxuan Qiu,Bin Yang

DOI: https://doi.org/10.21203/rs.3.rs-1570905/v1

2022-01-01

Abstract:Abstract Purpose: Zirconia is a kind of chemically stable material that is able to form a weak bond with resin. For the purpose of investigating the surface properties of SiO2–ZrO2 coating on zirconia and its bonding with resin.Methods: the translucent zirconia discs based on different surface treatments were named CT (control group), SB (sandblasting), C21, C11 and C12 groups (with SiO2: ZrO2 = 2: 1,1: 1 and 1: 2 coatings). The surface of translucent zirconia coating was analyzed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), surface roughness assessment (Ra), X-ray diffraction (XRD), water contact angle (WCA), fracture toughness (KIC), flexural strength (FS), translucence parameter (TP) and shear bond strength (SBS). A 2-way analysis of variance (ANOVA) for shear bond strength results and a 1-way ANOVA for other data were performed as statistical analysis.Results: The SEM images revealed the existence of SiO2 islands on the coated translucent zirconia. The Ra of C12, C11, and C21 groups was larger than that of SB and CT groups. The XRD showed that phase transformation was not detected in any group. In addition, sandblasting and SiO2–ZrO2 coatings couldn’t reduce certain physical properties of translucent zirconia, but could reduce the WCA. According to the TP results, the translucency of the group C21 decreased, as well as group C11 illustrated the highest shear bond strength under both aging conditions.Conclusion: The SiO2–ZrO2 coating is a promising method to enhance the bonding between resin cement and translucent zirconia.