Influence of Surface Treatments on the Shear Bond Strength of Repaired Composite Resin to Zirconia-based All-ceramic

殷家悦,包扬,艾红军,司文捷

2009-01-01

Abstract:Objective:To evaluate the effect of different surface treatments on the bond strength between composite resin and zirconia core material.Methods:Sixty yttrium-stabilized tetragonal zirconium polycrystal(Y-TZP) blocks were fabricated and randomly assigned to six groups.Then five surface treatments were performed:acid etching with 8% hydrofluoric acid(H);airborne-particle abrasion(A);silica coating(S);H+S;A+S;no treatment(N) as a control group.Composite resin were bonded onto the Y-TZP rectanglars.After 24 hours at 37℃ distilled water storage,all Y-TZP/resin specimens were subjected to a shear load until fracture occurred.Scanning electron microscope(SEM) was used to inspect the surface characterization of different trentments.Result:The mean values in MPa±SD of shear bond strength test for group A(33.45±3.46)and AS(36.95±2.93)were statistically higher than other groups(P<0.01).No significant differences were detected in N,H,S and HS groups.And no statistically significance existed between silica coating groups and no-silica coating groups under the same treatment.SEM showed that acid etching with 8% hydrofluoric acid has no effect on Y-TZP surface structure but the Y-TZP surface could be modified significantly by airborne-particle abrasion.Conclusion:Airborne-particle abrasion was the most effective surface treatment in terms of bond strength increase;Acid etching with 8% hydrofluoric acid and silica coating had a poor influence on the bond strength between Y-TZP and repaired composite resin.