Abstract:Here, the effect of temperature on the electrochemical corrosion of 316L stainless steel (SS) in methyl diethanolamine (MDEA) solution with/without 1.0 wt.% NaCl in the presence/absence of CO2 was investigated using potentiostatic polarization, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS). The electrochemical measurements showed that although the MDEA solution was highly basic, both chloride and temperature played greater roles in the pitting corrosion of 316L SS, similar to plain NaCl solution. The critical pitting temperature (CPT) of 316L SS in MDEA solution with 1.0 wt.% NaCl decreased from 67.2 oC to 59.6 oC, and the breakdown potential underwent a negative shift of approximately 400 mV, and the EIS Bode impedance decreased. Furthermore, the breakdown potential shifted negatively with increasing temperature when the temperature was lower than CPT in the MDEA solution containing Cl−; however, the breakdown potential decreased slowly, and its temperature dependence was unclear when the temperature was higher than the CPT. In addition, the passive film resistance of 316L SS in all MDEA solutions decreased as the temperature increased. Particularly for the MDEA solution containing Cl−, the passive film resistance decreased by one order of magnitude when the temperature increased from 50 °C to 60 °C. Although the presence of CO2 in the MDEA solution decreased the passive film resistance, it seemed to reduce the individual corrosion contribution of Cl−. The pitting corrosion process of 316L SS in MDEA solution containing chloride ions was discussed by combining these results with classical pitting mechanisms of stainless steel.

Corrosion Resistance of Steel Materials in LiCl-KCl Melts

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Corrosion Behavior of 20G and TP347H in Molten LiCl-NaCl-KCl Salt

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Effect of Temperature and Impurity Content to Control Corrosion of 316 Stainless Steel in Molten KCl-MgCl2 Salt

Corrosion behavior of iron-based and Ni-based alloys melted in NaCl–MgCl 2 –KCl mixed molten salt under vacuum atmosphere

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

Corrosion behavior and mechanism of 316 stainless steel in NaCl–KCl–FeCl3 molten salt and vapor at 300°C

Corrosion behavior of carburized 316 stainless steel in molten chloride salts

Corrosion Behaviors of TWIP Steels in NaCl Solution

Corrosion and electrochemical investigations for stainless steels in molten Solar Salt: The influence of chloride impurity

Corrosion behaviors and protective layer stabilization mechanism of 316 stainless steel in NaCl–KCl–NaF reciprocal salts at high temperatures

Corrosion Behavior of Carbon Steel in LiCl/H2O Mixtures

Corrosion mechanism of additively manufactured 316 L stainless steel in 3.5 wt.% NaCl solution

Corrosion behavior and mechanism of 316 stainless steel in NaCl-KCl-ZnCl2 molten salts at high temperature

High temperature corrosion behaviour of the 316 stainless steel in NaCl-KCl-AlCl 3 molten salt and its vapour

Corrosion Behavior of Candidate Structural Materials for Molten Salt Reactors in Flowing NaCl-MgCl2

Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700°C

Effect of temperature on the electrochemical pitting corrosion behavior of 316L stainless steel in chloride-containing MDEA solution

Study on Corrosion Behavior of China low activation Ferritic/martensitic Steel in Static Liquid Lithium