Microstructures and mechanical properties of (TiBw+Ti 5 Si 3 )/TC11 composites fabricated by hot isostatic pressing and subjected to 2D forging
Yu Fu,Yongdong Xu,Yinyang Wang,Yu Bai,Hai Hao,Xiurong Zhu
DOI: https://doi.org/10.1016/j.jallcom.2023.171523
IF: 6.2
2023-08-05
Journal of Alloys and Compounds
Abstract:In this study, microstructures and mechanical properties of (TiBw+Ti 5 Si 3 )/TC11 composites fabricated by hot isostatic pressing and 2D forging were investigated. A α + β titanium alloy TC11 (Ti-6.4Al-3.5Mo-1.4Zr-0.25Si) was used as a matrix material. The TiB 2 addition corresponding to 5.0 and 3.5 vol% of TiB w and the Si addition corresponding to 2.0, 4.0 and 6.0 vol% of Ti 5 Si 3 were used as additives to the TC11 titanium alloy. TiB w and Ti 5 Si 3 reinforced TC11 titanium matrix composites were fabricated by hot isostatic pressing and 2D forging in the α + β temperature field at T = 980 °C. The microstructure of the as-forged composites was composed of nanoscale Ti 5 Si 3 particle within the β-phase and TiB w around TC11 matrix particle. The TiB w reinforcer tend to be distributed along the stretching deformation direction. Compared with the TC11 matrix alloy, the strength of the (2Ti 5 Si 3 +5TiB w )/TC11 composite after 2D forging at room temperature increased by about 90 MPa due to the fine-grain strengthening of the α-phase, the precipitation strengthening of the nanoscale Ti 5 Si 3 silicide, and the load transfer efficiency of TiB w . The main failure mechanism of the composites at room temperature is fracture of TiB w followed by ductile failure of the matrix. (2Ti 5 Si 3 +5TiB w )/TC11 is thought as the optimal choice for engineering application, which UTS and El. at 600 °C are 851 MPa and 11%, respectively, and corresponding values of parameters at 750 °C are 385 MPa and 21%, respectively. Compared to the maximum service temperature 500 °C of TC11 alloy, the service temperature of (2Ti 5 Si 3 +5TiB w )/TC11 composite can be improved by over 100 °C while retaining the similar tensile strength and elongation.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering