Abstract:Silicon carbide (SiC) is an effective material for high-temperature engineering applications owing to its desirable properties such as high elastic modulus, high hardness, and melting temperature, high thermal conductivity, good corrosion and oxidation resistance, low density, and coefficient of thermal expansion compared with other advanced ceramics. Nevertheless, poor sinterability and low toughness limit its use, which can be overcome using appropriate additives. In this study, the effect of different amounts of nano-β-SiC (0, 5, 10, and 15 wt.%) and graphene (0, 1, 2, and 3 wt.%) particles on the sinterability behavior and microstructure of SiC composite has been investigated. After weighing, dispersing nano-β-SiC and graphene, and mixing the starting materials, milling was carried out at 180 rpm for 3 h. The materials obtained were then compressed uniaxially under a pressure of 75 MPa and then were compressed again through CIP under 150 MPa. To remove volatile products, the pyrolysis process was performed at 800 °C under Ar atmosphere. Finally, the samples were sintered at 2200 °C for 2 h by the pressureless sintering process. XRD analysis was used to investigate the phases and FESEM images were used to study the microstructure. According to the XRD patterns, β-SiC particles were converted to α-SiC, which was accompanied by the elongation of SiC grains. Also, no reaction was observed between graphene and the SiC matrix. According to the FESEM images, the samples containing 5 wt.% nano-β-SiC and 1 wt.% graphene showed a uniform distribution of reinforcement particles but with increasing the amount of the reinforcement particles, agglomeration was observed. According to the results, upon increasing the nano-β-SiC up to 5 wt% and graphene up to 1 wt.%, all the measured properties including relative density, and linear shrinkage improved and reached 99.04%, and 18.01%, respectively. However, with increasing the additives, these properties deteriorated due to increasing porosity and agglomeration in the composite structure.

High-pressure and High-Temperature Sintering of Pure Cubic Silicon Carbide: A Study on Stress–strain and Densification

Investigation of the effect of pressure, sintering temperature and time on silicon carbide microstructure

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Study on the Performance for Silicon Carbide Ceramics by Hot-pressing Sintering

PRESSURELESS SINTERING OF SILICON CARBIDE NANOCOMPOSITE CERAMICS

Pressure Sintering, Structure and Some Properties of SiC–Al Composite Materials

Pressureless Sintering of Microporous Silicon Carbide Ceramics

Production of silicon carbide reinforced molybdenum disilicide composites using high-pressure sintering

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Microstructure and mechanical properties of spark plasma sintered SiC ceramics aided by B4C

Enhanced toughness and hardness at cryogenic temperatures of silicon carbide sintered by SPS

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Aqueous Processing, Hot-Pressing and Mechanical Properties of Silicon Carbide with Al2O3 and Y2O3

Pressureless sintering of SiC matrix composites reinforced with nano-β-SiC and graphene

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Sintering Behavior, Microstructure and Mechanical Properties of Silicon Carbide Ceramics Containing Different Nano-Tin Additive

Preparation, microstructure and ion-irradiation damage behavior of Al4SiC4-added SiC ceramics

Cubic silicon carbide under tensile pressure: Spinodal instability

High-temperature tensile behavior of 3D SiC/SiC composites

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles