Abstract:Mg-RE (magnesium-rare earth) alloys exhibit pronounced in-plane anisotropy of mechanical response under quasi-static monotonic loading resulting from the RE texture, as extensively reported. In this work, an obvious in-plane anisotropy of cyclic deformation behavior was observed in an extruded Mg-3Y alloy sheet during strain-controlled tension-compression low-cycle fatigue (LCF) at room temperature. The extrusion direction (ED) samples displayed better fatigue resistance with almost symmetrical hysteresis loops and longer fatigue life compared with the transverse direction (TD) samples. The influences of texture on the deformation modes, cracking modes, and mechanical behavior of Mg-Y alloy sheets under cyclic loading were studied quantitatively and statistically. The activation of various slip/twinning-detwinning systems was measured at desired fatigue stages via EBSD observations together with in-grain misorientation axes (IGMA) analysis. The results indicate that the activation of deformation modes in the TD sample was featured by the cyclic transition, i.e., prismatic slip (at the tensile interval) →{10–12}tension twinning (at the compressive reversal) → detwinning + prismatic slip (at the re-tensile reversal). In the case of the ED sample, the cyclic deformation was dominated by the basal slip throughout the fatigue life. For cracking modes, intergranular cracking and persistent slip bands (PSB) cracking were the primary cracking modes in the ED sample while the TD sample showed a high tendency of {10–12} tension twinning cracking (TTW cracking). The underlying mechanisms influencing the activation of various slip/twinning-detwinning systems, as well as cracking modes and cyclic mechanical behavior, were discussed.

Quantitative Investigation on the Deformation Modes and Cracking Behavior During Cyclic Torsional Loading of Extruded Pure Mg and Mg-3y Alloy

Cyclic Shear Deformation and Fatigue of Extruded Mg-Gd-Y Magnesium Alloy

Anisotropic cyclic deformation behavior of an extruded Mg-3Y alloy sheet with rare earth texture

The deformation modes and transferability during low-cycle fatigue of Mg and Mg–3Y alloy

Effect of yttrium addition on dynamic mechanical properties, microstructure, and fracture behavior of extrusion-shear ZC61 + xY (x = 0, 1, 2, 3) alloys

Constitutive Modeling of Slip, Twinning and Detwinning for Mg Alloy and Inhomogeneous Evolution of Microstructure

Quantitative study on the influence of strain amplitude on deformation mechanisms and cracking modes during cyclic torsion of AZ31 magnesium alloy

Quantitative Investigation on the Slip/Twinning Activity and Cracking Behavior During Low-Cycle Fatigue of an Extruded Mg-3Y Sheet

Cyclic Deformation And Correspondent Crack Initiation At Low-Stress Amplitudes In Mg-Gd-Y-Zr Alloy

A Study of Fatigue Damage Development in Extruded Mg–Gd–Y Magnesium Alloy

In-Situ Analysis of the Tensile Deformation Modes and Anisotropy of Extruded Mg-10gd-3y-0.5zr (wt.%) at Elevated Temperatures

Quantitative Study on Slip/twinning Activity and Theoretical Critical Shear Strength of Mg Alloy with Y Addition

Small Crack Behavior of Extruded Mg-Gd-Y-Zr Alloy under High Cycle Fatigue

Observation of Non-Basal Slip in Mg-Y by in Situ Three-Dimensional X-ray Diffraction

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

Effects of Y on the Deformation Mechanisms of Extruded Mg-Y Sheets During Room-Temperature Compression

Double-peak Strain Hardening Behavior of Mg–1.2 wt.%Y Alloy

In-Situ Study on the Tensile Deformation and Fracture Mechanism of a Bimodal-Structured Mg-Gd-Y Alloy

In Situ Monitoring of Dislocation, Twinning, and Detwinning Modes in an Extruded Magnesium Alloy under Cyclic Loading Conditions

Cyclic Deformation Behavior of a Rare-Earth Containing Extruded Magnesium Alloy: Effect of Heat Treatment

Strain Hardening Behavior of Mg–Y Alloys after Extrusion Process