Systematical factor analysis of dendrite morphology and solute distribution in entire welding molten pool of Al Cu alloy: An MPF-LBM study
Xiangbo Liu,Jinwei Long,Xinwei Du,Jiasi Cai,Yanhong Wei
DOI: https://doi.org/10.1016/j.jmapro.2024.05.035
IF: 5.684
2024-05-20
Journal of Manufacturing Processes
Abstract:The microstructure of fusion weld is significantly affected by factors like the welding process, heterogeneous nucleation, and initial grain morphology. Existing phase field studies on these factors mostly encounter challenges in considering the melt flowing in the molten pool and its direct effect on solute transport and dendrite motion, and their reliability in guiding microstructure and product quality control during manufacturing remains to be improved. This work established a multiphase field-lattice Boltzmann model to systematically reinvestigate the effects of these factors on the weld microstructure. The complete solidification process of the entire moving molten pool with a large number of dendrites was simulated and most classic physical phenomena, such as fluid flow, solution convection, heterogeneous nucleation, dendritic solid motion, and CET, were realized in our simulation. The simulation results are in better agreement with the microstructure of the actual weld. Systematic comparative phase field simulations were performed to analyze the effect of various factors affecting the dendrite morphology and solute distribution in welds when the melt flow is considered. The results show that the melt flowing creates a solute vortex at the end of the molten pool, accelerates the growth of upstream columnar dendrites, and exacerbates the asymmetry of equiaxed dendrites. The size of the solute vortex, the growth rate of columnar dendrites, and the asymmetry of equiaxed dendrites are positively related to the top tangential velocity. Reducing the temperature gradient increases dendrite size, causes accumulation of residual liquid, and intensifies the asymmetry of the equiaxed dendrites. Reducing the welding speed increases the final grain size and the number of narrow equiaxed dendrites. Increasing the maximum nucleation density and mean nucleation undercooling by increasing the density and size of the modifier respectively can adjust the weld from a coarse columnar dendrite structure to a fine equiaxed dendrite structure.
engineering, manufacturing