Abstract:Irradiation assisted stress corrosion cracking (IASCC) of austenitic stainless steel core components is one major concern for maintenance of nuclear power plants. Previous studies on the IASCC had mainly focused on the effect of irradiation on changes in deformation modes and interaction of dislocation channels with grain boundary. The role of corrosion in IASCC, however, has not received sufficient attentions. In the process of stress corrosion cracking (SCC), corrosion occurs simultaneously with localized deformation in the vicinity of the crack tip. This indicates that corrosion is one of the potential contributors to IASCC. In this work, IASCC of proton-irradiated nuclear grade 304 stainless steel (304SS) was investigated. The IASCC tests were conducted by interrupted slow strain rate tensile (SSRT) tests at 320 degrees C in simulated primary water of pressurized water reactor containing 1200 mg/L B as H3BO3 and 2.3 mg/L Li as LiOH center dot H2O, with a dissolved hydrogen concentration of 2.6 mg/L. Following the SSRT tests, the localized deformation, corrosion and IASCC of the specimens were characterized. The results revealed that increasing the irradiation dose promoted residual strain accumulation at slip steps and grain boundaries of nuclear grade 304SS. Since the slip step usually transmitted or terminated at the grain boundary, it eventually promoted localized deformation at the grain boundary. Specially, the slip step transmitted at grain boundary led to slip continuity at the grain boundary. In contrast, a slip discontinuity was observed at the grain boundary where the slip step terminated, which caused a much higher strain accumulation by feeding dislocations to the grain boundary region. Further, formation of the slip discontinuity was related to the Schmidt factor pair type of the adjacent grains. The irradiation resulted in a depletion of Cr and an enrichment of Ni at grain boundary, while the magnitude of Cr depletion and Ni enrichment increased with increasing the irradiation dose. Following the SSRT tests, intergranular cracking was observed on surfaces of the irradiated specimens, while the number of the cracks was increased by a higher irradiation dose and applied strain. This suggested a higher IASCC susceptibility of nuclear grade 304SS in the primary water. Meanwhile, significant intergranular oxidation ahead of the crack tip was observed, while both the width and length of the oxide were larger at a higher irradiation dose. The synergic effect of irradiation-promoted deformation and intergranular corrosion was the primary cause for the IASCC of the irradiated steel.

Effect of Surface State on Corrosion and Stress Corrosion for Nuclear Materials

Research Trends on Micro and Nano-Scale Materials Degradation in Nuclear Power Plant

Effects of Surface Grinding for Scratched Alloy 690TT Tube in PWR Nuclear Power Plant: Microstructure and Stress Corrosion Cracking

Key Problems On The Mechanical Behavior Of Nuclear Materials And Structures Of Pressured Water Reactors

Proton Irradiation Assisted Localized Corrosion and Stress Corrosion Cracking in 304 Nuclear Grade Stainless Steel in Simulated Primary PWR Water

A Review on the Behavior of 308L Cladding Material and Their Corrosion in Nuclear Power Plants

Corrosion Mechanisms of Stainless Steel and Nickel Base Alloys in High Temperature High Pressure Water

Study on Irradiation Assisted Stress Corrosion Cracking of Nuclear Grade 304 Stainless Steel

Corrosion Behavior and Mechanism of Irradiated 304 Nuclear Grade Stainless Steel in High-Temperature Water

Surface stability in stress-assisted corrosion: a peridynamic investigation

CORROSION FATIGUE OF NUCLEAR-GRADE STAIN- LESS STEEL IN HIGH TEMPERATURE WATER AND ITS ENVIRONMENTAL FATIGUE DESIGN MODEL

Effect of Irradiation on Corrosion of 304 Nuclear Grade Stainless Steel in Simulated PWR Primary Water

Detrimental Effect of Surface Mechanical Grinding on Stress Corrosion Behavior of Monel 400 alloy in Hydrofluoric Acid Vapor

Research Progress of Crevice Corrosion and Crevice Corrosion Issues of Nuclear-grade Materials

Corrosion behaviour of nanocrystallines 304 stainless steel in simulated secondary side environment

Microscopic Analysis of Intergranular Corrosion of 316L Stainless Steel

Errosion-Corrosion Critical Performance of Surface Nanocrystalline 20 Carbon Steel in Condensate Water

Understanding Stress Corrosion Cracking (SCC), Affecting Variables and Prevention Strategies in Nuclear Power Plants—A Review

Review of Stress Corrosion Cracking of Structural Materials in Nuclear Power Plants

The Effect of Surface Grinding on the Stress Corrosion Cracking Initiation of 316LN Stainless Steel in 600oc Supercritical CO2

Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone