A Revisit to the Role of Mo in an MP35N Superalloy:An Experimental and Theoretical Study

Qing Cheng,Jinyong Mo,Xiaoqing Li,Xiandong Xu

DOI: https://doi.org/10.1016/j.jmst.2023.01.017

2023-01-01

Journal of Material Science and Technology

Abstract:Molybdenum(Mo)has been recognized as an essential alloying element of the MP35N(Co35.4Cr22.9Ni35.5Mo6.2,at.％)superalloy for enhancing strength and corrosion resistance.However,a full understanding of the addition of Mo on microstructure and mechanical properties of the Mo-free parent alloy is lacking.In this work,we consider five(Co37.7Cr24.4Ni37.9)100-xMOx(x=0,0.7,2.0,3.2,and 6.2)alloys,and reveal that yield/tensile strength and ductility are continuously increased for these alloys with increasing Mo content while a single-phase face-centered cubic structure remains unchanged.It is found that strong solid solution strengthening(SSS)is a main domain to the improved yield strength,whereas grain boundaries are found to soften by the Mo addition.The first-principles calculations demonstrate that a severe local lattice distortion contributes to the enhanced SSS,and the grain boundary softening effect is mostly associated with the decreased shear modulus.Both first-principles calculations and scanning transmission electron microscopy observations reveal that the stacking fault energy(SFE)reduces by the Mo addition.The calculated SFE value decreases from 0.4 mJ/m2 to-11.8 mJ/m2 at 0 K as Mo content increases from 0 at.％to 6.2 at.％,and experimentally measured values of SFE at room temperature for both samples are about 18 mJ/m2 and 9 mJ/m2,respectively.The reduction of SFE promoted the generation of stacking faults and deformation twins,which sustain a high strain hardening rate,thus postponing necking instability and enhancing tensile strength and elongation.