Abstract:The long-term oxidation kinetics of the P92 steel and iron aluminide diffusion coating formed on its surface by the pack cementation process have been investigated at 650 °C over a period of more than 7000 h both in 100% steam and in air under normal one atmospheric pressure by intermittent weight measurement at room temperature. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) techniques were used to analyse the oxidised surfaces. For the P92 steel substrate, the scale formed by oxidation is largely magnetite (Fe 3 O 4 ) in steam and haematite (Fe 2 O 3 ) in air. Despite this difference in the type of oxide scales formed, it was found that the long-term oxidation kinetics of the P92 steel substrate in both steam and air can be described by a logarithmic time relationship: Δm t = k l ln( t/t° + 1); the constants k l and t ° were subsequently determined using a closest fit process for oxidations in steam and air. For the coating, the oxide scale formed in both steam and air was Al 2 O 3 , which provided the long-term oxidation resistance. It was observed that the long-term oxidation kinetics of the coating in both steam and air can be best described by Δm t = Δm 0 + k c t 1/3 ; the rate constant k c of oxidation in steam and air was then determined by the least squares method. For both the P92 steel substrate and coating, the rate of oxidation is faster in steam than in air at 650 °C particularly in the case of the P92 steel substrate.

Dissolution Behaviour of Laves Phase in P92 High Alloy Steel in Alkaline Solutions

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500$^\circ$C

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Electrochemical Characterization Method of Laves Phase in 9Cr Martensitic Heat-Resistant Steel and Creep Life Prediction

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Long-term oxidation kinetics of aluminide coatings on alloy steels by low temperature pack cementation process

Dissolution corrosion of FeCrAl alloy exposed to oxygen-depleted lead-bismuth eutectic containing Ni impurities at 600 °C

Precipitation and Coarsening of Laves Phases in T92 Steels in the Process of Creep

Microstructural Evolution of P92 Steel with Different Creep Life Consumptions After Long-Term Service

Liquid metal embrittlement susceptibility of an oxide-dispersion strengthened FeCrAl alloy in contact with liquid lead-bismuth eutectic at 350 °C

Introduction Of L1(2)-Ordered Precipitation To Alumina-Forming Austenitic Heat-Resistant Steels With Low Ni Content

Corrosion Behavior of Laves Precipitates in Fecral-1nb Alloy at 290°C and 7 Mpa: the Size Effect and Critical Role of Ph

Introduction of L12-Ordered Precipitation to Alumina-Forming Austenitic Heat-Resistant Steels with Low Ni Content

Low-temperature Formation and Steam Oxidation of Β-Feal Coating on P92 Steel

Investigating the real-time dissolution of a compositionally complex alloy using inline ICP and correlation with XPS

Low-energy Electron-Driven Observation of Nanometer-Sized Laves Phases at Alloy Surfaces Enabling Statistical Characterization with High Precision and Efficiency

Impact of L1(2)-Ordered Precipitation on the Strength of Alumina-Forming Austenitic Heat-Resistant Steels

Effects of Alloy Elements on Oxidation Resistance and Stress-Rupture Property of P92 Steel

Oxidation and dissolution behavior of FeCrNiAl based high entropy alloy and alumina-forming austenitic steel exposed to lead-bismuth eutectic (LBE)