Microstructure and properties of powder metallurgy martensitic-austenitic composite steel

LI Jingyu,WANG Yaomin,JIANG Feng,LI Yanguo,YANG Zhinan,ZHANG Fucheng

DOI: https://doi.org/10.13228/j.boyuan.issn1006-6543.20220030

2023-01-01

Abstract:In recent years, the demand for high-strength-high-plasticity metal materials in the fields of automobiles and ships has been increasing. In order to obtain high-strength-high-plasticity metal materials, powder metallurgy technology plays an increasingly important role. In this study, the mixed metal powders of martensitic steel and austenitic steel with a mass ratio of 2:1 were sintered by spark plasma sintering（SPS）, and the austenite phase was uniformly distributed in the martensite phase. The density of the sample is as high as 95.5%, and through the subsequent hot rolling treatment, the sintering quality of the composite steel is improved, and the density is increased to98.9%.The yield strength, tensile strength, uniform elongation and total elongation of the clad steel after hot rolling are 960 MPa, 1 529 MPa, 6.7% and 6.7%, respectively. On the basis of hot rolling, cold rolling + short-time high temperature tempering treatment is introduced, and the performance of powder metallurgy composite steel is further improved. Among them, the clad steel cold-rolled at 30%-500℃ and tempered for 5 min has yield strength,tensile strength, uniform elongation and total elongation of 1 899 MPa, 1 964 MPa, 9.2% and 10.0%, respectively.