Non-isothermal reduction kinetics of biomass carbon-coated spherical iron oxide nanoparticles

HAO Suju,LIU Zheng,JIANG Wufeng,BO He,GAO Yice,ZHANG yuzhu

DOI: https://doi.org/10.13228/j.boyuan.issn1006-6543.20220055

2023-01-01

Abstract:The TG-DTA curve of carbon-coated spherical nano-iron oxide in N 2 atmosphere was drew by high temperature comprehensive thermal analyzer. The thermogravimetric variation of carbon-coated spherical nano-iron oxide at different heating rates was analyzed. The reaction mechanism of carbon-coated spherical nano-iron oxide in N2 atmosphere was studied and its dynamic parameters were got. Ironic nitrate nonahydrate and urea were used as raw materials to control the formation of spherical nano-iron oxide by hydrothermal method, and carbonized biomass glucose by hydrothermal carbonization to prepare carbon-coated spherical nano-iron oxide. The kinetic parameters of carbon-coated spherical nano-iron oxide reduction were determined by mutual verification by Flynn-Wall-Ozawa method and Coats-Redfern method. Spherical nano-iron oxide was successfully prepared by hydrothermal method,and carbon-coated spherical nano-iron oxide was successfully prepared by hydrothermal carbonization using biomass glucose as carbon source. The reaction process of carbon-coated spherical nano-iron oxide under N 2 atmosphere was determined by kinetic analysis, as well as its reaction activation energy and reaction model. The results show that the reaction between coated biomass carbon and nano-iron oxide can occur at 180 °C, the reduction temperature is reduced. With the increase of temperature, the CO generated by the reaction will continue to participate in the reaction, accelerating the reduction of spherical nano-iron oxide. The reaction activation energy is about 79.48 kJ/mol, and the reaction model is a three-dimensional diffusion model.