Abstract:The truncated octahedral LiNi0.08Mn1.92O4 (LNMO) cathode material with dominant {111}, truncated {110} and {100} crystal planes was prepared by a low temperature solid-state combustion method. The dominant {111} crystal plane of the unique truncated octahedron can form firm solid electrolyte interphase (SEI) layer and alleviate the manganese dissolution during the discharge-charge process, and a small part of {110} and {100} crystal planes can increase the rapid diffusion channels of Li+ ions. The field emission scanning electron microscope (SEM) and X-ray diffractometer (XRD) results show that LNMO has cubic spinel structure with submicron particle size. The electrochemical performances of LNMO are also outstanding at high temperature of 55 degrees C, the initial discharge capacities are 109.9 and 98.0 mAh/g with capacity retentions of 75.8% and 80.5% after 300 cycles at 1 and 5 C, respectively. Even at high current rates of 10 and 15 C, the capacity retentions of 48.4% and 49.4% have been maintained after 1000 cycles, while the capacity loss of undoped LiMn2O4 is as high as 98% after 1000 cycles at 15 C. Moreover, the dynamic performance tests show that LNMO owns larger Li+ diffusion coefficient (D=3.86x10(-15) cm(2)/s), smaller charge transfer resistances (before cycle and after cycles, the R-ct=158.0 and 279.8 Omega) and lower apparent activation energy (E-a=17.63 kJ/mol) than LiMn2O4 (LMO), demostrate its enhanced Li+ transport dynamic. The XRD tests of two electrode slices after 1000 cycles at 10 C show that the crystal structure of LNMO electrode material is almost unchanged, which indicated that the Ni doping and the truncated octahedral structure of particles could improve the structural stability of material, effectively inhibit the Jahn-Teller effect and Mn dissolution, remarkably improve its high temperature electrochemical performance. Therefore, this work provides a reference for the application of spinel LiMn2O4 electrode material at high temperature.

Preparation of Long Cycle Lifespan Spinel LiMn2O4 Cathode Material by a Dual-Modified Strategy

Radially Oriented Single‐Crystal Primary Nanosheets Enable Ultrahigh Rate and Cycling Properties of LiNi0.8Co0.1Mn0.1O2 Cathode Material for Lithium‐Ion Batteries

Boosting High-Rate Capacity and Long-Cycle Stability of Spinel LiMn2O4 by the Cr-Al Co-Doping Strategy

Improved long cycle performance of LiMn<sub>2</sub>O<sub>4</sub> cathode material by Ni-B co-doping combined with truncated octahedron morphology

Improved Capacity Retention and Ultralong Cycle Performance of Ni-Fe Co-Doped LiMn2O4 Cathode Material at High Current Densities

From the Crystal Inside to the Surface: A Completely Activated Spinel LiMn 2O 4 Cathode Material with a High Rate and Long-Life Behavior

Stimulative formation of truncated octahedral LiMn2O4 by Cr and Al co-doping for use in durable cycling Li-ion batteries

Enhanced High-Rate and Long-Cycle Performance of Mg2+-Al3+ Co-Doped Spinel LiMn2O4 Cathode Materials for Li-ion Batteries

Preparation and Long Cycle Electrochemical Properties of B-Doped Spinel LiMn<sub>2</sub>O<sub>4</sub> Cathode Material

Improving Fast-Charging Capability of High-Voltage Spinel LiNi0.5Mn1.5O4 Cathode under Long-Term Cyclability Through Co-Doping Strategy

Regulation of morphology evolution and Mn dissolution for ultra-long cycled spinel LiMn<sub>2</sub>O<sub>4</sub> cathode materials by B-doping

Preparation of LiMn2O4 Cathode with Excellent Cycling Performance

Improved Electrochemical Performance of Spinel LiNi0.5Mn1.5O4 Cathode Materials with a Dual Structure Triggered by LiF at Low Calcination Temperature

Preparation and High Temperature Electrochemical Performance of LiNi0.08Mn1.92O4 Cathode Material of Submicron Truncated Octahedron

Correlating Cycle Performance Improvement and Structural Alleviation in LiMn2-xMxO4 Spinel Cathode Materials: A Systematic Study on the Effects of Metal-Ion Doping

Effects of Cr3+ Doping on Spinel LiMn2O4 Morphology and Electrochemical Performance

High-rate and Long-Life Performance of a Truncated Spinel Cathode Material with Off-Stoichiometric Composition at Elevated Temperature

Facile Synthesis of LiMn2O4 Octahedral Nanoparticles As Cathode Materials for High Capacity Lithium Ion Batteries with Long Cycle Life

Preparation and electrochemical properties of Al‐F co‐doped spinel LiMn 2 O 4 single‐crystal material for lithium‐ion battery

Regulation of Morphology and Particle Size of Spinel LiMn2O4 Induced by Fe-B Co-Doping for High-Power Lithium Ion Batteries

Bulk and surface reconstructed Li-rich Mn-based cathode material for lithium ion batteries with eliminating irreversible capacity loss