Preparation and Long Cycle Electrochemical Properties of B-Doped Spinel LiMn₂O₄ Cathode Material

Liu Qing,Guo Jun-Ming,Liu Xiao-Fang,Bai Hong-Li,Xiang Ming-Wu,Bai Wei,Duan Kai-Jiao

DOI: https://doi.org/10.11862/CJIC.2021.046

2021-01-01

Chinese journal of inorganic chemistry

Abstract:A single crystal polyhedron LiMn1.94B0.06O4 cathode material was prepared by a solid-state combustion synthesis, their structural and electrochemical properties were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and charge-discharge test. The results show that B-doping did not change the crystal structure of spinel LiMn2O4, and it could promote the preferential growth of (440) and (400) crystal facets. Inducing the formation of the single crystal polyhedron LiMn1.94B0.06O4 material with the highly exposed (111) facets and a small part of (110) and (100) facets, as well as a particle size of 160 similar to 350 nm, which enabled minimal Mil dissolution and provided more lithium ions channels. The LiMn1.94B0.06O4 delivered the initial discharge capacity of 103 mAh.g(-1) with a good capacity retention rate of 57.7% after 2 000 cycles at 10C and 25 degrees C. At high current rate of 15C, it showed the initial discharge capacity of 67.1 mAh.g(-1), and the capacity retention rates of 46.2% was obtained after 1 500 cycles. Moreover, at 1C and high temperature of 55 degrees C, the initial discharge capacity of 125.2 mAh.g(-1) was also maintained, showing good high temperature performance. The B-doping can effectively improve the high rate performance and cycle life of spinet LiMn2O4, stabilize the crystal structure, inhibit the Jahn-Teller effect and relieve the Mn dissolution.