Effect of Zr-doping on the Structure and Magnetic Properties of YMnO 3 Ceramics

Feng Wan,Xiaojun Bai,Yaocen Wang,Ziyan Hao,Lei Gao,Jinlin Li,Nikolai S. Perov,Chongde Cao
DOI: https://doi.org/10.1007/s10854-023-10259-3
2023-01-01
Journal of Materials Science Materials in Electronics
Abstract:Effect of zirconium substitution on the structure and magnetic properties of YMnO 3 ceramics were widely studied and discussed in this work. The crystal structure of Y 1 − x Zr x MnO 3 ( x = 0.00, 0.05, 0.10) is hexagonal, and the lattice parameters reduce with the increase of doping amount. The average of grain size decreases from 0.403 μm to 0.356 μm as the Zr addition rises through SEM analysis. The magnetization of Y 1 − x Zr x MnO 3 increases as Zr doping concentration increased, and the spin glass state appears in the sample with x = 0.1 The magnetization evolution should be attributed to the Mn 4+ ions appeared when Zr was introduced to the Y sites of YMnO 3 . The increased Mn 4+ ion which is related to the interstitial oxygen anions led to the reduced effective magnetic moment. The Zr substitution may also have an effect on the magnetic frustration factor.
What problem does this paper attempt to address?