High-response H2 Sensing Performances of ZnO Nanosheets Modulated by Oxygen Vacancies

Shiyu Zhou,Wenjun Yan,Min Ling,Chengdu Liang

DOI: https://doi.org/10.1039/d3qi00331k

IF: 7.779

2023-01-01

Inorganic Chemistry Frontiers

Abstract:A facile solution reduction method of NaBH4 was developed to modulate the oxygen vacancies of ZnO nanosheets. The sample with richer oxygen vacancies exhibits a lower working temperature (150 °C) with a great response (38.2).

What problem does this paper attempt to address?

The Oxygen Vacancy Defect of ZnO/NiO Nanomaterials Improves Photocatalytic Performance and Ammonia Sensing Performance

Jiaqi Zhang,Jin Li

DOI: https://doi.org/10.3390/nano12030433

IF: 5.3

2022-01-27

Nanomaterials

Abstract:In this paper, ZnO/NiO composites rich in oxygen vacancies are prepared by the solvothermal method and reduction method. In the test, through the use of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscope (TEM), diffuse reflectance spectroscopy (DRS), photoluminescence spectroscopy (PL), and electron paramagnetic resonance (EPR), we effectively prove the existence of phase, morphology and oxygen vacancies in the material. Through the photocatalysis test and gas sensitivity test, it is found that 10% Ni doped OZN-10 has the best photocatalytic activity and gas sensitivity characteristics. The degradation rate of methylene blue (MB) was 98%. The gas sensitivity test shows that OZN-10 has good selectivity, good response performance (3000 ppm, 27,887%) and excellent response recovery time (response time: 50 s, recovery time: 5–7 s) for saturated NH3 gas at standard atmospheric pressure (101.325 KPa) and room temperature (25 °C). The synergistic effect of oxygen vacancy as the center of a trap and p–n heterojunction forming an electric potential field at the interface is explained, and the mechanism of improving photocatalysis and gas sensitivity is analyzed. This work will provide an innovative vision for dual-performance oxygen vacancy modification of heterojunctions through photocatalysis.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
ZnO Nanosheets Abundant in Oxygen Vacancies Derived from Metal‐Organic Frameworks for ppb‐Level Gas Sensing

Hongye Yuan,Saif Abdulla Ali Alateeqi Aljneibi,Jiaren Yuan,Yuxiang Wang,Hui Liu,Jie Fang,Chunhua Tang,Xiaohong Yan,Hong Cai,Yuandong Gu,Stephen John Pennycook,Jifang Tao,Dan Zhao

DOI: https://doi.org/10.1002/adma.201807161

IF: 29.4

2019-01-13

Advanced Materials

Abstract:Surmounting the inhomogeniety issue of gas sensors and realizing their reproducible ppb-level gas sensing are highly desirable for widespread deployments of sensors to build networks in applications of industrial safety and indoor/outdoor air quality monitoring. Herein, a strategy is proposed to substantially improve the surface homogeneity of sensing materials and gas sensing performance via chip-level pyrolysis of as-grown ZIF-L (ZIF stands for zeolitic imidazolate framework) films to porous and hierarchical zinc oxide (ZnO) nanosheets. A novel approach to generate adjustable oxygen vacancies is demonstrated, through which the electronic structure of sensing materials can be fine-tuned. Their presence is thoroughly verified by various techniques. The sensing results demonstrate that the resultant oxygen vacancy-abundant ZnO nanosheets exhibit significantly enhanced sensitivity and shortened response time toward ppb-level carbon monoxide (CO) and volatile organic compounds encompassing 1,3-butadiene, toluene, and tetrachloroethylene, which can be ascribed to several reasons including unpaired electrons, consequent bandgap narrowing, increased specific surface area, and hierarchical micro-mesoporous structures. This facile approach sheds light on the rational design of sensing materials via defect engineering, and can facilitate the mass production, commercialization, and large-scale deployments of sensors with controllable morphology and superior sensing performance targeted for ultratrace gas detection.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
High performance H 2 sensors based on NiO-SnO 2 nanosheets in temperature-pulsed operation mode

Mingjie Li,Wenxin Luo,Wenjun Yan

DOI: https://doi.org/10.1088/1361-665x/ad4cc1

IF: 4.1

2024-05-18

Smart Materials and Structures

Abstract:Enhancements in the responses of semiconductor gas sensors for hydrogen (H 2 ) are imperative to ensure the safety for industrial processes and fuel cells applications. Alternative to the conventional method of maintaining an optimum isothermal temperature, this study presents a novel technique that sequentially modulates the physisorption and chemisorption processes of the target gas and oxygen species through a temperature-pulsed strategy. This method substantially amplified the electrical responses of a NiO-doped SnO 2 gas sensor to H 2 vapor. Under the optimum pulsed-heating condition, the sensor achieved a remarkable response of 252 to 300 ppm H 2 , which is comparable to or better than that of many existing H 2 sensors. The integration of a pulse-driven microheater with a heterojunction-forming sensing layer has led to improved sensitivity, providing additional opportunities for H 2 monitoring.

materials science, multidisciplinary,instruments & instrumentation
In Situsolvothermal Reduction Engineering Enables Delicate Control over Surface-Rich Oxygen Vacancies on Bi2WO6for Highly Efficient Photocatalytic CO2reduction

Huanhuan Liu,Yanxu Chen,Wentao Wang,Xiaoyue He,ZiXu He,Lei Li,Suyuan Zeng,Ruiguo Cao,Genqiang Zhang

DOI: https://doi.org/10.1039/d3ey00019b

2023-01-01

Abstract:Anin situsolvothermal reduction strategy is proposed to precisely regulate the oxygen vacancy distribution of Bi2WO6in a refined control manner over programmable temperature, which shows a prominent photocatalytic CO evolution rate.
Enhanced low-working temperature 2-butanone gas-sensing performance of N-doped ZnO mesoporous nanosheets

Yukui Zhang,Yue Shen,Wenxiao Zhang,Zhichao Sun,Feng Gu,Linjun Wang

DOI: https://doi.org/10.1007/s10854-024-12284-2

2024-03-03

Journal of Materials Science Materials in Electronics

Abstract:In this work, N-doped ZnO (ZnON) mesoporous nanosheets were prepared via a two-step growth strategy, which consisted of a low temperature hydrothermal method and nitriding annealing process, and used to construct low-working temperature gas sensor for 2-Butanone selective detection successfully. The mesoporous nanosheets were characterized by XRD, SEM, BET, and XPS, and the effects of nitriding temperature on structure and gas sensitivity were discussed. ZnON series materials still retained channel structure, while adding an additional absorption band in the range of 500–650 nm, which was generated by N-doping. The optimal nitriding temperature was 450 °C and the related ZnON-450 gas sensor had the best response to 2-butanone vapor at a low-working temperature of 130 °C, and the sensitivity to 100 ppm 2-butanone was 23.3, which was 19 times higher than that of pure ZnO-450. The enhanced gas-sensing performance of ZnON-450 was discussed, which could be attributed to the synergy effect of shallow energy levels introduced by N-doping, nucleophilic hanging groups of -NH 2 and specific mesoporous nanosheet structure. This work provides a promising route for the well development of low-working temperature N-doped electronic devices.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied
Thermal Annealing Induced Controllable Porosity and Photoactive Performance of 2D ZnO Sheets

Yuan-Chang Liang,Chen-Shiang Hung,Wei-Cheng Zhao

DOI: https://doi.org/10.3390/nano10071352

IF: 5.3

2020-07-11

Nanomaterials

Abstract:Porous ZnO sheets containing various degrees of a nanoscaled pore were successfully synthesized using a simple hydrothermal method and various postannealing procedures. The porosity features of the ZnO sheets can be easily tuned by changing both the annealing temperature and annealing atmosphere. The dense porous nature of ZnO sheets is beneficial to enhance light absorption. Moreover, the substantially increased oxygen vacancies in the ZnO sheets were observed especially after the hydrogen treatment as revealed in the X-ray photoelectron spectroscope and photoluminescence analyses. The high density of surface crystal defect enhanced the photoinduced electron-hole separation rate of the ZnO sheets, which is crucial for an improved photoactivity. The porous ZnO sheets formed at a hydrogen atmosphere exhibited superior photoactive performance than the porous ZnO sheets formed at the high-temperature ambient air annealing. The dense pores and massive crystal defects formed by a hydrogen atmosphere annealing in the ZnO crystals might account for the observed photoactive behaviors in this study.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
Porous and Single-Crystalline ZnO Nanobelts: Fabrication with Annealing Precursor Nanobelts, and Gas-Sensing and Optoelectronic Performance

Xiao-Bo Jin,Yi-Xiang Li,Yao Su,Zheng Guo,Cui-Ping Gu,Jia-Rui Huang,Fan-Li Meng,Xing-Jiu Huang,Min-Qiang Li,Jin-Huai Liu

DOI: https://doi.org/10.1088/0957-4484/27/35/355702

IF: 3.5

2016-01-01

Nanotechnology

Abstract:Porous and single-crystalline ZnO nanobelts have been prepared through annealing precursors of ZnSe · 0.5N2H4 well-defined and smooth nanobelts, which have been synthesized via a simple hydrothermal method. The composition and morphology evolutions with the calcination temperatures have been investigated in detail for as-prepared precursor nanobelts, suggesting that they can be easily transformed into ZnO nanobelts by preserving their initial morphology via calcination in air. In contrast, the obtained ZnO nanobelts are densely porous, owing to the thermal decomposition and oxidization of the precursor nanobelts. More importantly, the achieved porous ZnO nanobelts are single-crystalline, different from previously reported ones. Motivated by the intrinsic properties of the porous structure and good electronic transporting ability of single crystals, their gas-sensing performance has been further explored. It is demonstrated that porous ZnO single-crystalline nanobelts exhibit high response and repeatability toward volatile organic compounds, such as ethanol and acetone, with a short response/recovery time. Furthermore, their optoelectronic behaviors indicate that they can be promisingly employed to fabricate photoelectrochemical sensors.
Synthesis and H2 Gas-Sensing Property of ZnO Nanobelts

Wufeng Jiang,Suju Hao,Yuzhu Zhang,Yunhan Ling

DOI: https://doi.org/10.1149/ma2014-01/5/421

2014-01-01

ECS Meeting Abstracts

Abstract:ZnO nanostructures have been found to be of wide and diverse applications, such as field effect transistors, dye-sensitized solar cell, photoelectric devices and gas sensors, etc. ZnO nanostructures with different dimension various morphologies, including to nanowires, nanorods, nanotubes, nanoflowers and nanobelts have successfully synthesized by means of different methods. Comparing with other nanostructures, ZnO nanobelts have specific properties. A simple and effective method for the preparation of ZnO nanobelts was introduced in this paper. By using the electrochemical oxidation and heat treatment method,a layer of ZnO nanobelts thin film was obtained on the surface of Sn. In the first, the Sn-Zn alloy films were anodized in 0.01 M·L-1 of oxalic acid solution, and then the prepared films were annealed at 500°C for 2h in air ambient. The samples were characterized by field emission scanning electron microscopy (FE-SEM), Energy Dispersive X-Ray Spectroscopy (EDS) and X-ray diffraction (XRD). The results show that the ZnO nanobelts have a thickness of 20 nm, with widths of 200 nm and lengths of 1~5 μm. The H2 gas sensing property of the ZnO nanobelts was measured in a static apparatus at room temperature. It was found that the ZnO nanobelts exhibited excellent H2 compounds sensing property.
Enhanced H-2 Sensitivity At Room Temperature Of Zno Nanowires Functionalized By Pd Nanoparticles

Shoutian Ren,Guanghua Fan,Shiliang Qu,Qiang Wang

DOI: https://doi.org/10.1063/1.3647310

IF: 2.877

2011-01-01

Journal of Applied Physics

Abstract:For sensitive detection of H-2, ZnO nanowires networks decorated with photo-decomposed Pd nano-particles were fabricated between femtosecond laser-writing interdigitated electrodes by chemical vapor deposition method. When H-2 concentration is increased from 20 to 4000 ppm at room temperature, sensitivity of the sample is increased from 3.7% to 1017.9%. The high sensitivity can be explained by considering the reaction between the adsorbed O-2(-) and the disassociated H atoms facilitated by Pd nanoparticles. This mechanism is further supported by the H-2 response results under UV light illumination, which can reduce the amount of O-2(-) on the ZnO surface, leading to depressed sensitivity. The sensor also shows high selectivity, long-term stability, and ultra-low power consumption of nanowatt level, due to the novel fabrication process. (C) 2011 American Institute of Physics. [doi:10.1063/1.3647310]
Enhanced gas sensing performance of Li-doped ZnO nanoparticle film by the synergistic effect of oxygen interstitials and oxygen vacancies

Jianwei Zhao,Changsheng Xie,Li Yang,Shunping Zhang,Guozhu Zhang,Ziming Cai

DOI: https://doi.org/10.1016/j.apsusc.2014.12.194

IF: 6.7

2015-03-01

Applied Surface Science

Abstract:Li doped ZnO (Zn1−xLixO) nanoparticles with different content were synthesized. X-ray photoelectron spectroscopy (XPS) indicated that the ratio of oxygen to zinc for ZnO increased with increasing of Li content from x=0 to 0.2, which had been attributed to the introduction of oxygen interstitial by Li dopant. The sensing performance and the temperature-dependent conductivity were investigated. It is observed that Li doped ZnO showed higher sensitivity and selectivity compared to the undoped ZnO. The 0.1 Li doped ZnO performed the maximum responses of 71.5 and 40.2 for 100ppm methanol and formaldehyde, respectively, at 350°C. The research showed that the oxygen vacancies served as active sites which supported the oxygen adsorption and reaction, oxygen interstitials served as active sites to oxidize the reducing gases and produce electrons. The enhanced sensing performance of Li doped ZnO was attributed to the synergistic effect of oxygen interstitials and oxygen vacancies.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Facile Synthesis of Mesoporous ZnO Sheets Assembled by Small Nanoparticles for Enhanced NO2 Sensing Performance at Room Temperature

Ruosong Chen,Jing Wang,Lan Xiang

DOI: https://doi.org/10.1016/j.snb.2018.05.005

IF: 9.221

2018-01-01

Sensors and Actuators B Chemical

Abstract:Here we demonstrate a facile synthesis of nanoparticle-assembled mesoporous ZnO sheets by calcination of a novel sheet-like delta-Zn(OH)(2) precursor at low temperature (100 degrees C). The mesoporous ZnO sheets were assembled by ultrasmall ZnO nanoparticles with an average crystal size less than 10 nm, having a high specific surface area of 87.63 m(2) g(-1). The high specific surface area, rich mesopores and oxygen vacancies, and the small crystal size of the ZnO nanoparticles contributed to the good NO2 sensing performance of the sensors. The comparison study indicated that the mesoporous ZnO sheets assembled by the smallest nanoparticles exhibited the highest response to ppm level of NO2 at room temperature (the response to 1 ppm of NO2 was 135%). Moreover, the sensor exhibited high response/recovery rates, full reversibility and good selectivity to NO2. Based on the surface depletion model, the higher response of the mesoporous ZnO sheets assembled by the smaller nanoparticles was attributed to their more significant narrowing of the conduction channel upon exposure to NO2. (C) 2018 Published by Elsevier B.V.
Oxygen Vacancies in ZnO Nanosheets Enhance CO2 Electrochemical Reduction to CO

Zhigang Geng,Xiangdong Kong,Weiwei Chen,Hongyang Su,Yan Liu,Fan Cai,Guoxiong Wang,Jie Zeng

DOI: https://doi.org/10.1002/anie.201711255

2018-05-22

Abstract:As electron transfer to CO2 is generally considered to be the critical step during the activation of CO2 , it is important to develop approaches to engineer the electronic properties of catalysts to improve their performance in CO2 electrochemical reduction. Herein, we developed an efficient strategy to facilitate CO2 activation by introducing oxygen vacancies into electrocatalysts with electronic-rich surface. ZnO nanosheets rich in oxygen vacancies exhibited a current density of -16.1 mA cm-2 with a Faradaic efficiency of 83 % for CO production. Based on density functional theory (DFT) calculations, the introduction of oxygen vacancies increased the charge density of ZnO around the valence band maximum, resulting in the enhanced activation of CO2 . Mechanistic studies further revealed that the enhancement of CO production by introducing oxygen vacancies into ZnO nanosheets originated from the increased binding strength of CO2 and the eased CO2 activation.
ZnO Nanorods with Doubly Positive Oxygen Vacancies for Efficient Xylene Sensing

Hui Yang,Ming-Mei Zhao,Lan Li,Le-Xi Zhang

DOI: https://doi.org/10.1021/acsanm.1c04146

IF: 6.14

2022-02-19

ACS Applied Nano Materials

Abstract:Because of their structural flexibility, earth abundance, and environmental friendliness, ZnO nanomaterials have been widely utilized for gas sensors. ZnO-based sensors showed a high gas response performance, which can be essentially attributed to the effect of oxygen vacancies. However, rare research has focused on the type of oxygen deficiency for regulating gas sensing properties. In this work, we first synthesized ZnO nanorods with a low BET surface area of 6.8 m2/g, presenting superior normalized gas sensitivity toward 200 ppm xylene. This was attributed to very high amounts of doubly positively charged oxygen vacancies forming in these nanorods by creating a highly anoxic environment for oxygen-deficient ZnO growth. In contrast, Ga doping can serve as active sites that are beneficial for adsorbing more oxygen into the lattices of ZnO, resulting in a reduced number of doubly positively charged oxygen vacancies, lower oxygen vacancy-related photoluminescence intensity, and worse xylene sensing performance. Therefore, the doubly positively charged oxygen vacancies play an important role in the gas sensing performance of metal-oxide semiconductors. The results obtained can provide a strategy and facilitate research on the design of other metal-oxide semiconductors with gas sensing properties.

materials science, multidisciplinary,nanoscience & nanotechnology
Ultralow detection limit MEMS hydrogen sensor based on SnO2 with oxygen vacancies

Na Luo,Chen Wang,Dan Zhang,Mengmeng Guo,Xiaohong Wang,Zhixuan Cheng,Jiaqiang Xu,Na Luo,Chen Wang,Dan Zhang,Mengmeng Guo,Xiaohong Wang,Zhixuan Cheng,Jiaqiang Xu

DOI: https://doi.org/10.1016/j.snb.2021.130982

2022-03-01

Abstract:Controllable and efficient construction of oxygen vacancies on the surface of metal oxide semiconductors (MOSs) is essential for their application in the gas sensor. Herein, a general H2 reduction method is developed to synthesize SnO2 with oxygen vacancies defect (SnO2-D) by annealing the SnO2 in a H2 atmosphere at different temperature (300 °C, 400 °C and 500 °C), and then named SnO2-D3, SnO2-D4 and SnO2-D5, respectively. It was found that although the determined specific surface areas for pristine SnO2, SnO2-D3, SnO2-D4 and SnO2-D5 are 103.749 m2g−1, 63.316 m2g−1, 47.652 m2g−1 and 15.541 m2g−1, respectively, the gas sensitivity test results indicate that the SnO2-D4 Micro-Electro-Mechanical System (MEMS) sensor shows improved response and excellent low-concentration detection capability (down to 0.1 ppm) to H2 compared with that fabricated with pristine SnO2, SnO2-D3 and SnO2-D5. The abnormal relationship between specific surface area and gas sensing performance is attributed to the more oxygen vacancies of SnO2-D4 surface. In addition, ZnO (ZnO-D) and In2O3 (In2O3-D) with oxygen vacancy defects based on the H2 reduction method show better gas sensitivity than ZnO and In2O3 sensors, which further proves that oxygen vacancy defects can effectively improve the gas-sensing performance of MOSs.

chemistry, analytical,electrochemistry,instruments & instrumentation
Oxygen vacancy engineering of zinc oxide for boosting piezo-electrocatalytic hydrogen evolution

Xin Xiong,Yang Wang,Jiangping Ma,Yingxin He,Jingyan Huang,Yajie Feng,Chaogang Ban,Li-Yong Gan,Xiaoyuan Zhou

DOI: https://doi.org/10.1016/j.apsusc.2023.156556

IF: 6.7

2023-01-30

Applied Surface Science

Abstract:Vibration-driven piezo-electrocatalytic hydrogen evolution reaction has drawn great interest in the past years as it provides an effective approach to harvest the dispersed and extensive mechanical energy. However, its wide applications remain a grand challenge due to the unsatisfied catalytic activity of currently available piezo-electrocatalysts. Here, the defect engineering is applied in the hydrothermally-synthesized ZnO by heat treatment to fabricate ZnO catalysts with various concentrations of oxygen vacancy. Under the stimulation of ultrasonic vibration, ZnO with optimal oxygen vacancy concentration shows a piezo-electrocatalytic H 2 yield of 3.8 mmol · h −1 · g −1 . The controlled experiments of piezo-current response and electrochemical impedance spectroscopy disclose that the piezo-generated carriers' separation and transfer are greatly enhanced in ZnO after introducing oxygen vacancies. Density functional theory calculations uncover that the oxygen vacancies of ZnO play an important role in facilitating H desorption. This work delivers an efficient strategy to achieve the simultaneous improvement of carrier dynamics and surface reaction and ultimately promote piezo-electrocatalytic H 2 evolution.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Oxygen vacancy modulation of two-dimensional γ-Ga2O3 nanosheets as efficient catalysts for photocatalytic hydrogen evolution

Xiaoyan Zhang,Zizhong Zhang,Huijuan Huang,Ying Wang,Na Tong,Jinjin Lin,Dan Liu,Xuxu Wang

DOI: https://doi.org/10.1039/c8nr07186a

IF: 6.7

2018-12-07

Nanoscale

Abstract:Controlling the creation of oxygen vacancies can effectively regulate the optical and electronic properties of metal oxide nanomaterials. Over the past several decades, numerous metal oxides with oxygen vacancies have been developed. However, an investigation about oxygen vacancies leading to the formation of nanosheets with different thicknesses has not been available up to now. Here, we report the oxygen vacancy modulated formation of γ-Ga2O3 nanosheets and demonstrate that the thickness of the nanosheets is not the decisive factor in the photocatalytic hydrogen evolution reaction of ultrathin 2D nanosheets. Detailed structural characterization indicated that γ-Ga2O3 prepared at 160 °C (γ-160) with a morphology of ultrathin nanosheets possesses the highest oxygen vacancy concentration and an optimal thickness of the nanosheets. The enhanced photocatalytic performance could be determined from the synergistic effects between the ultrathin 2D structure and the O-vacancies confined in the ultrathin nanosheets. This work provides an efficient strategy to regulate the formation of nanosheets at the atomic scale and enrich the study on the effect of oxygen vacancies in the photocatalytic water splitting reaction.
High-Response Room-Temperature NO2 Sensor and Ultrafast Humidity Sensor Based on SnO2 with Rich Oxygen Vacancy.

Yujia Zhong,WeiWei Li,Xuanliang Zhao,Xin Jiang,Shuyuan Lin,Zhen,Wenduo Chen,Dan Xie,Hongwei Zhu

DOI: https://doi.org/10.1021/acsami.9b01737

IF: 9.5

2019-01-01

ACS Applied Materials & Interfaces

Abstract:SnO2 nanosheets with abundant vacancies (designated as SnO2- x) have been successfully prepared by annealing SnSe nanosheets in Argon. The transmission electron microscopy results of the prepared SnO2 nanosheets indicated that high-density SnO2- x nanoplates with the size of 5-10 nm were distributed on the surface of amorphous carbon. After annealing, the acquired SnO2- x/amorphous carbon retained the square morphology. The stoichiometric ratio of Sn/O = 1:1.55 confirmed that oxygen vacancies were abundant in SnO2 nanosheets. The prepared SnO2- x exhibited excellent performance of sensing NO2 at room temperature. The response of the SnO2- x-based sensor to 5 ppm NO2 was determined to be 16 with the response time and recovery time of 331 and 1057 s, respectively, which is superior to those of most reported room-temperature NO2 sensors based on SnO2 and other materials. When the humidity varied from 30 to 40%, Δ R/ R was 0.025. The ultrafast humidity response (52 ms) and recovery (140 ms) are competitive compared with other state-of-art humidity sensors. According to the mechanistic study, the excellent sensing performance of SnO2- x is attributed to its special structure.
Unraveling the Effect of Oxygen Vacancy on WO 3 Surface for Efficient NO 2 Detection at Low Temperature

Ruixia Li,Qiao Wang,Yanrong Wang,Beixi An,Yifan Yang,Zhengkun Wu,Peizhe Wang,Tingyu Zhang,Ruiqi Han,Erqing Xie

DOI: https://doi.org/10.1021/acsami.4c11801

IF: 9.5

2024-09-13

ACS Applied Materials & Interfaces

Abstract:Oxygen vacancies (V(O)) in metal oxide semiconductors play an important role in improving gas-sensing performance of chemiresistive gas sensors. Nonetheless, there is still a lack of clear understanding of the inherent mechanism of the influence of oxygen vacancies on gas sensing due to generally focusing on the concentration of V(O). Herein, oxygen vacancies were rationally modulated in WO(3) nanoflower structures via an annealing process, resulting in a transformation of V(O) from neutral...

materials science, multidisciplinary,nanoscience & nanotechnology
Properties of ZnO with Oxygen Vacancies and Its Application in Humidity Sensor

Liyan Niu,Sulei Hong,MaoHua Wang

DOI: https://doi.org/10.1007/s11664-021-08966-w

IF: 2.1

2021-05-19

Journal of Electronic Materials

Abstract:Zinc oxide is one of the most popular oxide semiconductor materials. We have developed an exquisite and simple method for preparing ZnO with oxygen vacancies. X-ray diffraction, UV–Vis absorption spectroscopy, x-ray photoelectron spectroscopy, Raman spectroscopy and photoluminescence spectroscopy confirmed the existence of oxygen vacancies and the narrowing of the band gap. The optical band gap value is reduced from 3.28 eV to 3.07 eV. The modified ZnO has a different morphology from that of pure ZnO. The roughness of the sample is significantly increased and the size is reduced, and it shows better humidity performance. The results showed that modification with 0.5 M sodium borohydride increases the concentration of oxygen vacancy defects on the surface of ZnO, thus improving the sensitivity of the humidity sensor using the modified ZnO. We attributed this performance to the presence of oxygen vacancies and the increase in roughness, thereby enhancing dissociation and electrolytic conduction to provide more active sites for attachment. This study reveals the effect of reducing agents on regulating defects in metal-oxide semiconductor materials.

engineering, electrical & electronic,materials science, multidisciplinary,physics, applied
Oxygen Vacancy Induced Band-Gap Narrowing and Enhanced Visible Light Photocatalytic Activity of ZnO

Junpeng Wang,Zeyan Wang,Baibiao Huang,Yandong Ma,Yuanyuan Liu,Xiaoyan Qin,Xiaoyang Zhang,Ying Dai

DOI: https://doi.org/10.1021/am300835p

2012-07-23

Abstract:Oxygen vacancies in crystal have important impacts on the electronic properties of ZnO. With ZnO(2) as precursors, we introduce a high concentration of oxygen vacancies into ZnO successfully. The obtained ZnO exhibits a yellow color, and the absorption edge shifts to longer wavelength. Raman and XPS spectra reveal that the concentration of oxygen vacancies in the ZnO decreased when the samples are annealed at higher temperature in air. It is consistent with the theory calculation. The increasing of oxygen vacancies results in a narrowing bandgap and increases the visible light absorption of the ZnO. The narrowing bandgap can be confirmed by the enhancement of the photocurrent response when the ZnO was irradiated with visible light. The ZnO with oxygen vacancies are found to be efficient for photodecomposition of 2,4-dichlorophenol under visible light irradiation.

materials science, multidisciplinary,nanoscience & nanotechnology

High-response H2 Sensing Performances of ZnO Nanosheets Modulated by Oxygen Vacancies

The Oxygen Vacancy Defect of ZnO/NiO Nanomaterials Improves Photocatalytic Performance and Ammonia Sensing Performance

ZnO Nanosheets Abundant in Oxygen Vacancies Derived from Metal‐Organic Frameworks for ppb‐Level Gas Sensing

High performance H 2 sensors based on NiO-SnO 2 nanosheets in temperature-pulsed operation mode

In Situsolvothermal Reduction Engineering Enables Delicate Control over Surface-Rich Oxygen Vacancies on Bi2WO6for Highly Efficient Photocatalytic CO2reduction

Enhanced low-working temperature 2-butanone gas-sensing performance of N-doped ZnO mesoporous nanosheets

Thermal Annealing Induced Controllable Porosity and Photoactive Performance of 2D ZnO Sheets

Porous and Single-Crystalline ZnO Nanobelts: Fabrication with Annealing Precursor Nanobelts, and Gas-Sensing and Optoelectronic Performance

Synthesis and H2 Gas-Sensing Property of ZnO Nanobelts

Enhanced H-2 Sensitivity At Room Temperature Of Zno Nanowires Functionalized By Pd Nanoparticles

Enhanced gas sensing performance of Li-doped ZnO nanoparticle film by the synergistic effect of oxygen interstitials and oxygen vacancies

Facile Synthesis of Mesoporous ZnO Sheets Assembled by Small Nanoparticles for Enhanced NO2 Sensing Performance at Room Temperature

Oxygen Vacancies in ZnO Nanosheets Enhance CO2 Electrochemical Reduction to CO

ZnO Nanorods with Doubly Positive Oxygen Vacancies for Efficient Xylene Sensing

Ultralow detection limit MEMS hydrogen sensor based on SnO2 with oxygen vacancies

Oxygen vacancy engineering of zinc oxide for boosting piezo-electrocatalytic hydrogen evolution

Oxygen vacancy modulation of two-dimensional γ-Ga2O3 nanosheets as efficient catalysts for photocatalytic hydrogen evolution

High-Response Room-Temperature NO2 Sensor and Ultrafast Humidity Sensor Based on SnO2 with Rich Oxygen Vacancy.

Unraveling the Effect of Oxygen Vacancy on WO 3 Surface for Efficient NO 2 Detection at Low Temperature

Properties of ZnO with Oxygen Vacancies and Its Application in Humidity Sensor

Oxygen Vacancy Induced Band-Gap Narrowing and Enhanced Visible Light Photocatalytic Activity of ZnO