Abstract:In this work, N-doped activated carbon supported metallic nickel (Ni/NAC) catalysts were fabricated by two-step calcination method in N-2 atmosphere for liquid-phase hydrogenation of furfural (FAL). It was found that the pyrolysis temperature and amount of melamine as N doping source have important influence on N doping content and type in activated carbon (AC) support, resulting in the subsequently formed Ni nanoparticles on N-doped AC with different sizes and thus affording different catalytic hydrogenation activities. The results demonstrated that using N-doped AC with 1.0 g melamine at 1073 K in N-2 atmosphere as support, the obtained Ni/NAC at 873 K in N-2 atmosphere with Ni nanoparticle sizes of similar to 13.1 nm (denoted as Ni/NAC-1-1073) exhibits a N doping content of 3.65 at.% and a surface area of 561.2 m(2) g(-1) with a microporous structure. As catalyst for FAL hydrogenation, Ni/NAC-1-1073 demonstrated the best catalytic performance among all investigated catalysts, achieving almost 100% selectivity of tetrahydrofurfuryl alcohol (THFOL) with a complete FAL conversion at 353 K after 3 h reaction, while only 76.7% selectivity of THFOL with a FAL conversion of 86.4% was obtained using Ni/AC catalyst without N doping under the identical experimental conditions. Furthermore, it was found that almost 100% conversion of FAL to furfural alcohol (FOL) can be reached by transfer hydrogenation pathway in 2-proponal solvent using Ni/NAC-1-1073 at 413 K after 5 h reaction, whereas Ni/AC without N doping can only afford 30.2% conversion of FAL to FOL under the same conditions. The superior catalytic performance of Ni/NAC-11073 could be ascribed to a synergistic effect of nanosized Ni providing catalytic active sites, suitable N doping content and type in AC to promote catalytic performance, and advantageous structure characteristics of high surface area and porous structure favourable for the exposure of catalytic active sites and mass transport. (C) 2016 Elsevier B.V. All rights reserved.

Selective Hydrogenation of Furfural over Supported Nickel and Nickel Phosphide Catalysts

Selective Hydrogenation of Furfural to Furfuryl Alcohol Without External Hydrogen over N-doped Carbon Confined Co Catalysts

Catalytic Transfer Hydrogenation of Furfural to Furfuryl Alcohol by Cu-Pd/Al2O3 in Near-Critical Isopropanol

Selective Hydrogenation of Phthalic Anhydride to Phthalide over Supported Nickel Catalysts

Switchable Synthesis of Furfurylamine and Tetrahydrofurfurylamine from Furfuryl Alcohol over RANEY® Nickel

Selective hydrogenation of furfural and its derivative over bimetallic NiFe-based catalysts: Understanding the synergy between Ni sites and Ni–Fe alloy

Highly Selective Liquid-Phase Hydrogenation of Furfural over N-Doped Carbon Supported Metallic Nickel Catalyst under Mild Conditions

Theoretical study on the hydrogenation of furfural for furfuryl alcohol production over low Ni modified Cu catalysts

Selective Hydrogenation of Furfural over Pt Based and Pd Based Bimetallic Catalysts Supported on Modified Multiwalled Carbon Nanotubes (MWNT)

Investigation on the structure and performance of supported Ni nanoparticles for the hydrogenation of furfural

Selective hydrogenation of furfural to tetrahydrofurfuryl alcohol in isopropanol over hydrotalcite-derived nickel-based catalyst

Highly Efficient and Selective Hydrogenation of Biomass-Derived Furfural Using Interface-Active Rice Husk-Based Porous Carbon-Supported NiCu Alloy Catalysts

Selective Hydrogenation of the Carbonyls in Furfural and 5-Hydroxymethylfurfural Catalyzed by PtNi Alloy Supported on SBA-15 in Aqueous Solution Under Mild Conditions

Sulfonate Group Modified Ni Catalyst for Highly Efficient Liquid-Phase Selective Hydrogenation of Bio-Derived Furfural

Controlled hydrogenation of furfural to furfuryl alcohol or cyclopentanone over Ni–P under mild conditions

Nitrogen-doped carbon nanotubes-supported PdNiCo nanoparticles as a highly efficient catalyst for selective hydrogenation of furfural

Catalysts Derived from Nickel-Containing Layered Double Hydroxides for Aqueous-Phase Furfural Hydrogenation

Alloying Nickel with Phosphorus to Switch the Selective Conversion of Furfural from Furans to Cyclopentanones or 1,4-Pentanediol

Catalytic In-Situ Hydrogenation of Furfural over Bimetallic Cu–Ni Alloy Catalysts in Isopropanol

Influence of acidity on the catalytic performance of Ni2P in liquid-phase hydrodeoxygenation of furfural to 2-methylfuran

Single nickel atoms anchored on porous N-doped nanocarbon with dual reaction sites for highly-efficient transfer hydrogenation of furfural to furfuryl alcohol