Abstract:One approach to decreasing the environmental footprint of the construction industry is to replace ordinary Portland cement (OPC) with recycled slag and fly ash activated using alkaline materials. This article presents the outcomes of an experimental study that evaluated water absorption characteristics and strength development of mortar that uses blends of alkali-activated ASTM class F slag and fly ash binders. Mortar mixes were developed using three binder combinations: 100% slag and no fly ash (S1F0), 75% slag + 25% fly ash (S3F1), and 50% slag + 50% fly ash (S1F1). Slag and fly ash binders were activated using NaOH solution with molarity ranging from 10 mol/L to 16 mol/L mixed with sodium silicate solution. Two sets of samples were created, one set was immersed in an acidic medium after casting, which represented a closed environment, and the second was left in the lab exposed to air until the test day. For mortar cured in a closed system, the highest strength development during the first seven days after casting occurred in S1F0 mortar followed by S3F1, then S1F1. The observation indicates strength development is dominated by the fast reactivity of slag during the first 7 days. The pattern is similar for all NaOH activator concentrations evaluated in this study. Mortar samples with high slag content (S1F0 and S3F1) that were cured in air experienced a decrease in strength during the 28–90 day curing phase as the strength at the age of 90 days decreased relative to the strength at 28 days. However, S1F1 gained strength during the 28–90 day phase when NaOH molarity was the highest (16 mol/L). This is due to the dissolution and activation of fly ash at high solution alkalinity which contributed to the continued increase in strength. A strong linear correlation between the square root of time (t0.5) and water absorption existed in all activated mortars evaluated in the study, except for mortar samples prepared using NaOH with high concentration and the highest ratio of Na2SiO3/NaOH. Therefore, alkali-activated slag-based mortars share similar water capillary absorption characteristics with conventional cement-based mortar. It was found that increasing the NaOH concentration increases the global warming potential (gwp) and that the mix with the least environmental impact was the S1F1 developed using the lowest NaOH concentration of 10 mol/L and 50% fly ash.

The Efficiency of Borax As an Additive on Properties of One-Part Fly Ash/slag-Based Alkali-Activated Materials

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Effect of borax-modified activator on mechanical properties and drying shrinkage of alkali-activated slag/metakaolin mortar

The Effect of Blast Furnace Slag/Fly Ash Ratio on Setting, Strength, and Shrinkage of Alkali-Activated Pastes and Concretes

Influence of superplasticizers and retarders on the workability and strength of one-part alkali-activated fly ash/slag binders cured at room temperature

Alkali-activated binder based on red mud with class F fly ash and ground granulated blast-furnace slag under ambient temperature

Modification mechanism of flue gas desulfurization gypsum on fly ash and ground granulated blast-furnace slag alkali-activated materials: Promoting green cementitious material

The Effect of Superplasticizers on Eco-friendly Low-Energy One-Part Alkali-Activated Slag

Chloride Ions' Penetration of Fly Ash and Ground Granulated Blast Furnace Slags-Based Alkali-Activated Mortars

Effect of Solid Sodium Silicate on Workability, Hydration and Strength of Alkali-Activated GGBS/Fly Ash Paste

Experimental and Statistical Study on the Properties of Basic Oxygen Furnace Slag and Ground Granulated Blast Furnace Slag Based Alkali-Activated Mortar

Influence of Different Admixtures on the Mechanical and Durability Properties of One-Part Alkali-Activated Mortars

Study on the properties of alkali-activated phosphorus slag mortar mixed with granulated blast furnace slag/fly ash

Alkali-activated slag & fly ash as sustainable alternatives to OPC: Sorptivity and strength development characteristics of mortar

Fresh and Hardened Properties of Alkali-Activated Fly Ash/slag Binders: Effect of Fly Ash Source, Surface Area, and Additives

Assessment of the performance of alkali-activated slag/fly ash using liquid and solid activators: early-age properties and efflorescence

Effect of CaO on the shrinkage and microstructure of alkali-activated slag/fly ash microsphere

Mechanical Properties of Fly Ash–Slag Based Alkali-Activated Materials under the Low-Energy Consummation-Sealed Curing Condition

Effect of fly ash and gypsum on drying shrinkage and mechanical properties of one‐part alkali‐activated slag mortar

Structure, morphology and compressive strength of Alkali-activated mortars containing waste bottle glass nanoparticles

Study on the Compressive Strength and Reaction Mechanism of Alkali-Activated Geopolymer Materials Using Coal Gangue and Ground Granulated Blast Furnace Slag