Abstract:In recent years, alkali-activated mortar (AAM) has emerged as a promising alternative to ordinary Portland cement (OPC) due to concerns regarding the environmental impact resulting from cement production, which releases carbon dioxide and degrades the quality of the environment. To address these concerns, researchers have explored the addition of supplementary binder materials to enhance cement properties and mitigate pollution. The effectiveness of these binder materials depends heavily on their chemical composition and fineness. Notably, ground granulated blast furnace slag (GGBS) enhances the strength and durability of the cement. In response to the scarcity of river sand (RS), dredged marine sand (DMS) has gained popularity as a potential substitute within the civil engineering field. Furthermore, the integration of nanomaterials has shown promising improvements in the mechanical and microstructural properties of mortar. Therefore, this study aims to investigate the properties of mortar by incorporating nano silica (NS) within the range of 1% to 7%, varying the molarity from 2 M to 8 M, and substituting RS with DMS. The tests carried out encompass a range of evaluations, including compressive strength, flexural strength, SEM-EDS, XRD, UPV, RCPT, and carbonation analysis, to comprehensively assess the properties of the mortar. The study reveals that the AAM demonstrates optimal performance when 50% of RS is replaced by DMS in the absence of NS. Once this optimal point is determined, further analyses are conducted at this value while varying the concentrations of NS from 1–7%. The experimental results indicate that replacing 50% of RS with DMS and incorporating 6% NS leads to maximum compressive strength (49.2 MPa) and flexural strength (9.36 MPa) in the assessed properties. Furthermore, the incorporation of NS in GGBS-based AAM mixes enhances durability by improving resistance against chloride penetration, reducing water absorption, and minimizing carbonation diffusion. Additionally, the microstructural and mineralogical characterization of GGBS-NS-based AAM specimens demonstrates the formation of C-S-H and C-A-S-H gels as the end products of the reactions.

Influence of Different Admixtures on the Mechanical and Durability Properties of One-Part Alkali-Activated Mortars

Strength, Fracture and Durability Characteristics of Ambient Cured Alkali—Activated Mortars Incorporating High Calcium Industrial Wastes and Powdered Reagents

Performance of Fiber-Reinforced Alkali-Activated Mortar with/without Nano Silica and Nano Alumina

Formulation and characterization of cleaner one-part novel fly ash/lime-based alkali-activated material

The potential of one-part alkali-activated materials (AAMs) as a concrete patch mortar

Long-Term Performance and Durability of Heat-Treated Alkali-Activated Slag Mortar Containing Silica Fume

Rheological, Fresh State, and Strength Characteristics of Alkali-Activated Mortars Incorporating MgO and Carbon Nanoparticles

Studies on the performance of alkali-activated aluminosilicate geopolymer mortar against exposure to acid, sulfate, and elevated temperature

Effect of borax-modified activator on mechanical properties and drying shrinkage of alkali-activated slag/metakaolin mortar

Chloride Ions' Penetration of Fly Ash and Ground Granulated Blast Furnace Slags-Based Alkali-Activated Mortars

Factors affecting compressive strength and expansion due to alkali-silica reaction of fly ash-based alkaline activated mortar

Influence of Silica Modulus and Curing Temperature on the Strength of Alkali-Activated Volcanic Ash and Limestone Powder Mortar

Investigation on the properties of sustainable alkali-activated GGBS mortar with nano silica and dredged marine sand: Mechanical, microstructural and durability aspects

Insulating and fire‐resistant performance of slag and brick powder based one‐part alkali‐activated lightweight mortars

Rheology and alkali-silica reaction of alkali-activated slag mortars modified by fly ash microsphere: a comparative analysis to OPC mortars

Structure, morphology and compressive strength of Alkali-activated mortars containing waste bottle glass nanoparticles

Freeze-thaw cycle and abrasion resistance of alkali-activated FA and POFA-based mortars: Role of high volume GBFS incorporation

Silicomanganese fume-based alkali-activated mortar: experimental, statistical, and environmental impact studies

One-Part Alkali-Activated Materials: State of the Art and Perspectives

Approaches to enhance the carbonation resistance of fly ash and slag based alkali-activated mortar- experimental evaluations

A Comparative Study on the Influence of Nano and Micro Particles on the Workability and Mechanical Properties of Mortar Supplemented with Fly Ash