STUDY ON WATER CONVERSION LAW AND SOLIDIFICATION MECHA-NISM OF CEMENT-SLAG-FLY ASH SOLIDIFIED SILT

ZHANG Xiaofang,CHEN Ruimin,JIAN Wenbin

DOI: https://doi.org/10.13544/j.cnki.jeg.2020-378

2023-01-01

Abstract:This paper investigates the relationship between the mechanical strength of the cement-slag-fly ash solidified silt excited by gypsum and the evolution of the water conversion process, and aims to essentially reveal the curing mechanism. Both the unconfined compressive strength test（UCS） and direct shear strength test（DST）were conducted to explore the effects of cementslagfly ash ratio, curing agent dosage and curing age on the strength of solidified silt. In addition, the nuclear magnetic resonance（NMR）relaxation analysis, X-ray diffraction（XRD） and scanning electron microscopy（SEM）were applied to observe the soil-water characteristics and analyze the mineral composition and the microstructure of hydration products. From the test results, the functional relationships among unconfined compression strength（q u ）,shear strength parameters（c,tan φ） and the combined water content（C w ）were established. Results show that during 14 days of age, the strength of solidified soil with a higher cement ratio（20%） is significantly higher than that of the low cement ratio（5%）. The early developed strength effect can be attributed to hydrate formation and the greatly increasing amount of combined water. After 14 days, the strength of low cement solidified soil increases rapidly and exceeds the strength of high cement solidified soil. From the perspective of macro-mechanical strength in the specimen with higher cement content（20%）,the strength parameters（q u , c,tan φ）all show a linear growth relationship with curing age（lg t）,while the specimen with low cement content（5%）has a power function relationship with lg t. In contrast, from the perspective of microscopic water conversion, the relationship among the combined water content C w , the compressive strength and the shear strength are identical in high and low cement ratio solidified soil, where, q u -C w and tan φ-C w increase as a power function, and c-C w exists a linear relationship. The mechanical strength of solidified soil is not only related to the amount of combined water, but also to the structure of hydrate. The flocculated hydrate C-A-S-H gradually forms a spatial network structure, which makes the micropore structure denser and reduces the porosity.