Abstract:The fatigue behaviour of aerospace structural components is dominated by the time to grow from a small sub mm size flaw to a flaw of the order of a few mm. As such crack growth is dominated by the Region I growth of short cracks. Consequently management of the fleet requires that Region I short crack growth be both understood and predicted. Recent studies at the NASA Johnson Space Center have shown that the current ASTM testing standards can produce Region I da/dN versus K data that are a function of the test geometry and, as result, that similitude was not valid in Region I. As a result the NASA Johnson Space Center has abandoned these standards. Similar conclusions follow from recent Australian studies into cracking in 7050-T7451 aluminium alloy under variable amplitude loading. This research particularly focuses on the near threshold crack growth behaviour in 7050-T7451 aluminium Alloy, which is widely used in F/A-18 Hornet, the Super Hornet and the Joint Strike Fighter (F35). In order to understand the short crack growth behaviour, a fatigue test program in 7050-T7451 Aluminium Alloy specimens under repeated block loading was performed. The results show that the short crack growth rate (da/dN) versus K anomaly is due to forcing a relationship between them. It is also shown that this anomaly vanishes if crack growth is expressed using the Generalized Frost-Dugdale crack growth equation or the Hartman-Shijve crack growth equation. In order to investigate the effect of the stress concentration factor (Kt) on the crack growth rate, the growth of fatigue cracks from etched pits and machinery defects at a fastener hole under an operation RAAF load spectrum was analysed. The results of this study show that the Hartman-Schijve equation can be used to predict DSTO short crack growth tests data for both low and high Kt specimens. Crack growth under a representative combat and transport load spectrum was also studied. The characteristic stress intensity factor range Krms and the Effective Block Approach for analysing fatigue crack growth was conducted. Here it was found that the Krms effective block approach is a valid method for predicting crack growth under F-15 Eagle fighter aircraft and military transport spectra. The use of the fractal based crack growth equation was also evaluated. In this content it was found that fracture surfaces associated with the growth of cracks from small near micron initial defects can be treated as a fractal set and that crack growth conforms to a fractal crack growth equation. From this research, the growth of fatigue cracks from small pits, typically less than 20m, to long cracks, can be represented by the Generalized Frost-Dugdale crack growth equation and the Hartman-Schijve crack growth equation.

Fatigue Crack Growth Behavior and Failure Mechanism of Nickel-Based Alloy GH4169 under Biaxial Load Based on Fatigue Test of Cruciform Specimen

Fatigue Crack Propagation Life Prediction of GH4169 Under Biaxial Load Based on Cruciform Specimen

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

A Study of Fatigue Mesoscopic Elasto-Plastic Properties of a Nickel-Base Superalloy by Instrumented Microindentation Measurements

Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169 at 650 °C in Air

Micro-notch Size Effect on Small Fatigue Crack Propagation of Nickel-Based Superalloy GH4169

Fatigue Life Prediction of Nickel-Based GH4169 Alloy on the Basis of a Multi-Scale Crack Propagation Approach

Quantitative Assessment of Microstructural Damage for Interior Crack Initiation and High Cycle Fatigue Life Modeling

Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Fatigue crack nucleation behavior in nickel-based PM alloy

Effect of Stress Ratio on the Fatigue Crack Propagation Behavior of the Nickel-based GH4169 Alloy

Grain Size Effect on the Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169

High-temperature Fatigue Crack Propagation Study of Superalloy GH4169 by Single-Lens 3D Digital Image Correlation

A combined cyclic viscoplasticity and entropy generation approach for modelling fatigue crack growth behavior of nickel-based superalloy at high temperature

Fatigue Crack Growth in the Threshold Region

Study on Microstructure and Fatigue Properties of FGH96 Nickel-Based Superalloy

Isothermal and thermo-mechanical fatigue-crack-growth analysis of XH73M nickel alloy

Experimental and Numerical Investigation of High-Temperature Multi-Axial Fatigue

Evaluation of multiaxial fatigue life prediction criteria for Ni-based superalloy GH4169

Critical Plane Fatigue Modeling and Characterization of Single Crystal Nickel Superalloys

Multiaxial Fatigue Life Prediction Based on Nonlinear Continuum Damage Mechanics and Critical Plane Method