First-Principles Study of Ion Diffusions in CH3NH3PbI3 and (nh2)2chpbi3 for Perovskite Solar Cells
Jun Haruyama,Keitaro Sodeyama,Liyuan Han,Yoshitaka Tateyama
DOI: https://doi.org/10.1149/ma2016-02/15/1417
2016-01-01
ECS Meeting Abstracts
Abstract:Perovskite solar cells (PSCs), which photo-absorbing layer consists of organometal halide perovskites, have gotten much attention because of their rapidly increasing power conversion efficiencies (3.8% in 2009, but nowadays over 22% cell has appeared). [1, 2] Especially, lead halide perovskites such as CH3NH3PbI3 (MAPbI3) and (NH2)2CHPbI3 (FAPbI3) show remarkable properties for solar cell applications, e.g. high optical absorption coefficients and long diffusion lengths of both charge carriers. However, the current−voltage (J−V) curve of PSCs often depends on voltage sweep rates and sweep directions, [3, 4] which make the evaluation of conversion efficiency difficult. Recently, the rate-dependent J−V hysteresis, which is due to a slow process continued about seconds, was attributed to ionic diffusions in MAPbI3. [5] In this study, we calculated activation barriers of ion diffusions in tetragonal MAPbI3 and trigonal FAPbI3 by first-principles calculations. The vacancy migrations of I− anions in both perovskites show low barriers of 0.3 to 0.45 eV, which values indicate that MAPbI3 and FAPbI3 are ion conductors. Furthermore, MA+ and FA+ cations have rather low barriers c.a. 0.6 eV. The results strongly suggest that the not only anions but also molecular cations can migrate in the perovskites when a bias voltage is applied. Based on the dilute diffusion theory, we can expect that small vacancy concentrations suppress these ion conductions. In addition, we suggest that replacement of MA molecule with larger one is also able to reduce MA migrations and to prevent the degradation of PSC photo absorbers. [6] [1] A. Kojima, K. Teshima, Y. Shirai, and T. Miyasaka, J. Am. Chem. Soc., 131, 6050 (2009). [2] Best Research-Cell Efficiencies, National Renewable Energy Laboratory. http://www.nrel.gov/ncpv/images/efficiency_chart.jpg [3] A. Dualeh, T. Moehl, N. Tétreault, J. Teuscher, P. Gao, M. K. Nazeeruddin, M. Grätzel, ACS Nano, 8, 362 (2014). [4] H. J. Snaith, A. Abate, J. M. Ball, G. E. Eperon, T. Leijtens, N. K. Noel, S. D. Stranks, J. T.-W. Wang, K. Wojciechowski, W. Zhang, J. Phys. Chem. Lett., 5, 1511 (2014). [5] W. Tress, N. Marinova, T. Moehl, S. M. Zakeeruddin, M. K. Nazeeruddin, M. Grätzel, Energy Environ. Sci., 8, 995 (2015). [6] J. Haruyama, K. Sodeyama, L. Han, and Y. Tateyama, J. Am. Chem. Soc., 137, 10048 (2015).