Abstract:The effective characterization of the mechanical property degradation of turbine blades in service for ultra-long-term had a critical impact on the service safety and maintenance decisions of turbine blades. In this study, the microstructure observation and mechanical property study of K403 polycrystalline Ni-based superalloy turbine blade under four service times were carried out, using microstructure characterization methods to quantify the microstructure evolution of the superalloy at different parts of the turbine blade with increasing service time. The effects of the microstructure degradation of the superalloy under ultra-long-term service time on the mechanical properties of the turbine blade were analyzed. The results show that the microstructural degradation characteristics of the superalloy turbine blades under ultra-long-term service were strongly correlated with the spatial structural characteristics of the turbine blades after service, and it was found that the carbon elements and other elements inside and at the boundary of the carbide showed regular migration behavior with the increase of service time. The regular influence of microstructural degradation of superalloy turbine blades under ultra-long-term service time on their mechanical properties was demonstrated. These results can provide empirical support for the study of the predicted residual properties of nickel-based superalloy turbine blades under ultra-long-term service.

The Microstructural Degradation of Ni-Based Superalloys with Segregation under the Super-Gravity Condition

Microstructure Degradation of Service-Exposed Turbine Blades Made of Directionally Solidified DZ125 Superalloy

Effect of Aging Heat Treatment on Microstructure of Ni-based Single Crystal Superalloys

Characterization of the Microstructure Evolution and Microsegregation in A Ni-Based Superalloy under Super-High Thermal Gradient Directional Solidification

Microstructure Characterization of Ni-Based Superalloys During Thermal Exposure

Experimental Investigation and Modelling of Microstructure Degradation in a DS Ni-based Superalloy Using a Quantitative Cross-Correlation Analysis Method

Mechanical Degradation Behavior and Γ′ Coarsening Mechanism of a Ni-based Superalloy During Long-Term High-Temperature Thermal Exposure

Microstructures and homogenization behavior of a nickel-based superalloy used for 850¬Ý‚ÑÉ turbine disc prepared by electron beam smelting layered solidification

Phase Field Simulation of Alloying Element Segregation During Solidification of DD5 Nickel-Base Single Crystal Superalloy

Study on the Microstructure and Mechanical Property Degradation of Ni-Based Superalloy in Long-Term Service

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Microstructural Deterioration Mechanism of Directionally Solidified Ni-Based Superalloy Used in First-Stage Industrial Gas Turbine Blades after Ultra Long-Term Service

Microstructural Evolution and Compositional Homogenization of a Low Re-bearing Ni-based Single Crystal Superalloy During Through Progression of Heat Treatment

Segregation and homogenization for a new nickel-based superalloy

Solidification and Segregation Characteristics of Ni-Based Superalloy C700r-1 for Ultra-Supercritical Steam Turbine Rotor

The Unique Influence of 1000°C High-Speed Rotation Simulated Turbine Blade Working Conditions on Microstructural Degradation of Single-Crystal Superalloy Nialreru

An Overview of Thermal Exposure on Microstructural Degradation and Mechanical Properties in Ni-Based Single Crystal Superalloys

Degradation and Dislocation Evolution of the Nickel-Based Single Crystal Superalloy DD6 under the Coupling High-Speed Rotating and High Temperature Environments

Microstructure Evolution of a New Directionally Solidified Ni-based Superalloy after Long-Term Aging at 950 °C Upto 1 000 H

Processing, Microstructures and Mechanical Properties of a Ni-Based Single Crystal Superalloy

The dynamic recrystallization of the Ni-based superalloy under the supergravity stress and high temperature