Abstract:Laminated C/SiC(carbon fiber reinforced silicon carbide composites) has the complicated nature of composite failure which include cracks for void defects at the meso and micro scales, complex cracks propagation of tunnel cracks, matrix cracks, delaminations and fiber cracks, orthotropic, and pseudoplastic behavior. It has technical challenge to solve all of them for complicated-mechanics problems by using multi-scale methodology. This paper focused tackling it by a model that lies between macro and meso scales, and proposed a new conceptual 3D FE-PDM(Finite Element - Progressive Damage Method). 3D FE-PDM was validated by the experiments of low-velocity impact of 2D C/SiC and 3D needled C/SiC. Damage initiation and evolution were controlled by strain in order to preventing stress chaos which could occur as cracks leading local stress relief. The multi-linear constitutive relations were adopted in orthotropic directions. The coupled effects of stresses between in-plane and out-of-plane were computed by adding damage coefficients into stiffness matrix. Cohesive Zone Method was used for delamination. The PDM approach was introduced for the 3D elements for intralaminar and cohesive elements for the interfaces. A parametric inversion methodology was put forward to determine the model parameters iteratively by comparing simulation results with the load-time curves, damage CT details of the experiments. Validation implies that, with small number of parameters, 3D FE-PDM is able to predict damage initiation of each phase knee, damage evolution, and load-displacement curve with good convergence for the low-velocity impact case. 2D woven and 3D needled non-woven C/SiC both have impact energy threshold and different damage evolution types.

Dynamic Compressive Response and Fracture Mechanisms of ZrB2–SiC Ceramic Based on Discrete Element Method

Research on dynamic mechanical properties and damage model of ceramic materials under multi‐axial stress

The Dynamic Response of Brittle Materials under Impact Loading

3D Finite Element Simulation of Complex Static and Dynamic Fracture in Quasi-Brittle Materials

Experimental and theoretical investigation of failure mechanism in Al 2 O 3 /SiC composite under plane shock waves

Numerical Simulations of the Dynamic Compressive Properties of Ceramic Particle Reinforced Metal Matrix Composites

Deformation and fracture of SiCp/Al composites under complex loading conditions: A simulation study

Dynamic Response of Ceramic Shell for Titanium Investment Casting under High Strain-Rate SHPB Compression Load

Achieving synergy of load-carrying capability and damage tolerance in a ZrB2-SiC composite reinforced through discontinuous carbon fiber

A Quantitative Representation of Damage and Failure Response of 3D Textile SiC/SiC Ceramics Matrix Composites Subjected to Flexural Loading

Experimental and numerical studies on low-velocity impact of laminated C/SiC structures

Strength damage behavior analysis of silicon carbide(SiC) ceramic cylindrical shells under hydrostatic pressure based on the state-based peridynamics

In situ Observation of Compression Damage in a Three-Dimensional Braided Carbon Fiber Reinforced Carbon and Silicon Carbide (C/C-SiC) Ceramic Composite

Toughness Mechanism of Layered ZrB2 Based Composite Ceramic

Simulation of crack patterns in quasi-brittle materials under thermal shock using phase field and cohesive zone models

Crack Velocity- and Strain Rate- Dependent Dynamic Compressive Responses in Brittle Solids

Numerical Simulation of the Mechanical Properties and Fracture of SiCp/6061Al Composite Materials Based on Microstructure

Compressive Strength and Damage Mechanisms in Ceramic Materials. I. The Role of Subcritical Tensile Microfracture Processes in Compression Failure of Ceramics. II. Electron Channeling Study of Fracture in Alumina-Evidence for Crack Tip Plasticity.

Characterization of Ceramic Microstructure and Nanoindentation under Different Loads

Computer simulated experiments on fracture toughness of particle-dispersed composites

Dynamic Fracture and Dissipation Behaviors of Concrete at the Mesoscale