Abstract:Cu-ZnO-Al2O3 is the most widely applied catalyst for CO2 hydrogenation to methanol. However, it is still a challenge to produce methanol using this catalyst under low-temperature (<250 °C) and low-pressure (<10 bar) conditions with desirable yield and selectivity. In this work, by tuning the experimental processing parameters such as solvent, loading amount, and annealing temperature, highly improved ZnO nanoarray supported Cu-ZnO-Al2O3 catalysts have been successfully demonstrated. By using organic solvent (N,N-dimethylformamide (DMF), acetone, or isopropanol) for dip-coating loading process instead of deionized (DI) water, Cu-ZnO-Al2O3 nanocatalysts was comparatively better dispersed on the nanorod array support with populated and abundant active sites, thus enhancing the methanol yield. With the control of the loading amount and annealing temperature, finely distributed Cu nanoparticles were obtained on the ZnO nanorod surfaces to enhance the interactions between Cu and ZnO nanorod surfaces. Further improvement of the catalyst performance is demonstrated by tuning the reaction space velocity. At 200 °C and 10 bar conditions, the optimized catalyst achieved a methanol yield of 6.46 mol h−1 kg−1 with 100 % selectivity. The good stability after prolonged testing of the catalysts demonstrates the potential practical implementation. The in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) measurements under the 1 bar reveal that the CO2 hydrogenation to methanol on the ZnO nanoarray supported Cu-ZnO-Al2O3 catalyst follows the CO reaction pathway, due to the surface oxygen vacancies on ZnO nanorods which facilitate CO2 dissociation.

Tuning of Cu-ZnO Interaction on Nanoflower-Like Cu/ZnO Catalyst for the Hydrogenation of Methyl Acetate

Catalytic in Situ Hydrogenation of Fatty Acids into Fatty Alcohols over Cu-Based Catalysts with Methanol in Hydrothermal Media

CuZnCoOx Multifunctional Catalyst for in Situ Hydrogenation of 5-Hydroxymethylfurfural with Ethanol As Hydrogen Carrier

Strong Cu/ZnO Interfacial Interaction Induced by ZrO2 Promoter Suppressing the Ethanol Formation in Industrial Methanol Synthesis

An Effective CuZn–SiO2 Bimetallic Catalyst Prepared by Hydrolysis Precipitation Method for the Hydrogenation of Methyl Acetate to Ethanol

DUAL PROMOTION OF Cu/ZnO CATALYSTS MODIFIED BY ACETYLACETONE PRECURSORS FOR CO2 HYDROGENATION TO METHANOL

Influence of Catalyst Structure on Performance of Cu/Sio2 in Hydrogenation of Methyl Acetate

Effect of the Cu/SBA-15 catalyst preparation method on methyl acetate hydrogenation for ethanol production

Tuning Interfaces between Cu and Oxide via Atomic Layer Deposition Method for CO2 Hydrogenation to Methanol

Synthesis of a Cu@ZnO1-x/Al2O3 Catalyst with High-Density ZnO1-x-Cu Interfacial Sites for Enhanced CO2 Hydrogenation to Methanol

Tuning of Catalytic Dimethyl Adipate Hydrogenation by Changing Composition of Cu–ZnO–TiO 2 Catalysts

An Effective Cu-Ag/HMS Bimetallic Catalyst for Hydrogenation of Methyl Acetate to Ethanol

Preparation of Cu/ZnO/Al2O3 Catalysts in a Solvent-Free Routine for CO Hydrogenation

Sonochemical synthesis of Zn-promoted porous MgO-supported lamellar Cu catalysts for selective hydrogenation of dimethyl oxalate to ethanol and their long-term stability

Optimization and understanding of ZnO nanoarray supported Cu-ZnO-Al2O3 catalyst for enhanced CO2 -methanol conversion at low temperature and pressure

High-Performance Cu/ZnO/Al 2 O 3 Catalysts for CO 2 Hydrogenation to Methanol

Enhanced Methanol Synthesis from CO 2 Hydrogenation Achieved by Tuning the Cu-ZnO Interaction in ZnO/Cu 2 O Nanocube Catalysts Supported on ZrO 2 and SiO 2

Effect of Mn promoter on Cu-based catalyst for hydrogenation of ethyl acetate to ethanol

Zn promoted Cu–Al catalyst for hydrogenation of ethyl acetate to alcohol

Synergistic interaction between Cu and ZrO2 promotes ethyl formate hydrogenation to produce methanol

The Role of Cu1-O3 Species in Single-Atom Cu Catalyst for Directional Methanol Synthesis from CO2 Hydrogenation