Gemological and Spectral Characteristics of HPHT Synthetic Rough Diamonds

ZHAO Chang,WANG Haikuo,LIU Yingxin

DOI: https://doi.org/10.3969/j.issn.1002-1442.2022.06.002

2022-01-01

Abstract:In this paper, a kind of catalyst type colorless HPHT synthetic diamond made by Hangzhou Huazuan New Material Technology Co., Ltd. was studied, hoping to provide the experimental basis for the identification and comparative study of different types of HPHT synthetic diamond. Experimental results show that the four samples are composed of octahedron {111}, cube {100}, trapezohedron {113} and rhombic dodecahedron {110}. Different surface features can be seen on the crystal surface, such as dendritic pattern, fern leaf pattern, almost parallel stripes, dotted and triangular pits, irregular pits, something similar to triangulum, stepped cleavage plane and irregular fracture planes. The samples showed strong blue fluorescence under Diamond ViewTM. Metal catalyst inclusions in the diamond crystal and black inclusions near the crystalline surface（100） can be seen by magnification examination, and the latter one is enriched in the metal elements of catalysts. The XRF analysis shows that Fe and Ni are the main catalysts metal elements, with Ca, Ti, Hf and Zr elements been added as "nitrogen removal agents". IR spectra indicate that the samples belong to IIa type diamond, and there are absorption peaks related to hydrogen element. The absorption peak of trace nitrogen at 270 nm was detected by UV-Vis spectrum with liquid nitrogen. Photoluminescence peaks related to Ni were both detected by 532 nm and 325 nm laser light sources（liquid nitrogen condition）. The deviation of Raman displacement and half peak width of the sample demonstrate there are limited difference between the samples and the standard diamond, indicating that the crystal quality of the samples is good.