Abstract:AbstractThe search for suitable friction materials for high-speed train is an attractive but difficult problem. In recent years, a variety of different novel friction materials were fabricated to meet the aims of high loads and speeds under ambient environment. Carbon fiber-reinforced carbon composites (C/C), carbon fiber-reinforced silicon carbide composites (C/C-SiC) and metallic composites fabricated by powder metallurgy are three excellent materials among them. Here a comparison of these three different materials working as brake pads, coupled with high-density C/C-SiC brake disk, was described. All the experiments were conducted using the same procedure with increasing initial braking speed (the rotation speed of brake disk at the beginning of braking process) from 30 to 59 m/s and constant load of 1.25 MPa, simulating the real working condition of high-speed train. The coefficient of friction (COF) and wear rates of three materials were compared and analyzed. During experiments, the COF of metallic and C/C pads remains nearly constant at 0.31 and 0.22, respectively, with increasing braking speed, while that of C/C-SiC exhibits a parabola. These different trends of COF may be attributed to the distinctive forming processes of friction film on the top of contact surfaces. Meanwhile, the wear rates of metallic composites increase rapidly from 683 to 1803 mm3/MJ with initial braking speed, while C/C-SiC presents the highest wear loss of 1887 mm3/MJ at 49 m/s and lowest value of 315 mm3/MJ at 59 m/s. Interestingly, the wear rate of C/C composites, due to the appropriate bonding strength of matrix/fiber and relatively high shear stress, decreases from 3698 to 903 mm3/MJ with increasing initial braking speed, which does not consist with pre-existing paper. Thus, metallic pads presented the lowest wear rates at lower speed (<49 m/s) but the highest at high speed, while C/C-SiC composite pads showed the greatest wear resistance at high speed. This investigation of three different friction materials will enhance our understanding of these friction materials and benefit the selection and safe application of high-speed train friction materials.

Effects of Aluminosilicate Particles on Tribological Performance and Friction Mechanism of Cu-matrix Pads for High-Speed Trains

Synergistic Effects of Different Graphite on the Braking Performance of Cu-Matrix Friction Materials for High-Speed Trains Based on Pin–Disc Tests

Effect of Surface Modification on the Tribological Properties of Friction Blocks in High-Speed Train Brake Systems

Effect of Type and Content of Iron Powder on the Formation of Oxidized Film and Tribological Properties of Cu-matrix Composites

Effect of Iron Powder Type on Friction and Wear Properties of Copper-Based Friction Powder Metallurgy Material

Tribological behavior and mechanism of h-BN modified copper metal matrix composites paired with C/C–SiC

Braking Performance of Fe-Based and Cu-Based Powder Metallurgy Pads Paired with C/C-SiC Disk on Full-Scale Dynamometer

Braking Performance of Copper-Based Friction Materials Reinforced by AlCoCrFeNi High-Entropy Alloy

Friction mechanism analysis of copper-based composites reinforced with ball-milled and modified composite ceramic powders

Friction and Wear Mechanics of Fe-Based PM Pad Paired with Carbon Fiber-Reinforced Silicon Carbide (C/C-SiC) Disk Under High-Speed Braking

Effect of Sintering Temperature on the Microstructure and Mechanical and Tribological Properties of Copper Matrix Composite for Brake Pads

Study on the Tribological Performance of Copper-Based Powder Metallurgical Friction Materials with Cu-Coated or Uncoated Graphite Particles as Lubricants

Influence of Braking Conditions on Tribological Performance of Copper-Based Powder Metallurgical Braking Material

Sliding Behavior and Particle Emissions of Cu-Free Friction Materials with Different Contents of Phenolic Resin

Braking behaviors of Cu-based PM brake pads mating with C/C–SiC and 30CrMnSi steel discs under high-energy braking

An experimental investigation on the tribological behavior of brake pads for high-speed trains in sandy environments

Tribological performance and composition optimization of semi-metallic friction materials applied for carbon ceramic brake disc

Comparison of Friction and Wear Behavior Between C/C, C/C-SiC and Metallic Composite Materials

Functionalization of alumina particles to improve the performance of eco-friendly brake-pads

Tribological behavior of aluminum matrix composites reinforced with ceramic particulates in dry sliding against a semimetallic friction material

Effect of Reinforcement on the Tribological Behavior of CuFe-Based Composites