Abstract:AbstractThe search for suitable friction materials for high-speed train is an attractive but difficult problem. In recent years, a variety of different novel friction materials were fabricated to meet the aims of high loads and speeds under ambient environment. Carbon fiber-reinforced carbon composites (C/C), carbon fiber-reinforced silicon carbide composites (C/C-SiC) and metallic composites fabricated by powder metallurgy are three excellent materials among them. Here a comparison of these three different materials working as brake pads, coupled with high-density C/C-SiC brake disk, was described. All the experiments were conducted using the same procedure with increasing initial braking speed (the rotation speed of brake disk at the beginning of braking process) from 30 to 59 m/s and constant load of 1.25 MPa, simulating the real working condition of high-speed train. The coefficient of friction (COF) and wear rates of three materials were compared and analyzed. During experiments, the COF of metallic and C/C pads remains nearly constant at 0.31 and 0.22, respectively, with increasing braking speed, while that of C/C-SiC exhibits a parabola. These different trends of COF may be attributed to the distinctive forming processes of friction film on the top of contact surfaces. Meanwhile, the wear rates of metallic composites increase rapidly from 683 to 1803 mm3/MJ with initial braking speed, while C/C-SiC presents the highest wear loss of 1887 mm3/MJ at 49 m/s and lowest value of 315 mm3/MJ at 59 m/s. Interestingly, the wear rate of C/C composites, due to the appropriate bonding strength of matrix/fiber and relatively high shear stress, decreases from 3698 to 903 mm3/MJ with increasing initial braking speed, which does not consist with pre-existing paper. Thus, metallic pads presented the lowest wear rates at lower speed (<49 m/s) but the highest at high speed, while C/C-SiC composite pads showed the greatest wear resistance at high speed. This investigation of three different friction materials will enhance our understanding of these friction materials and benefit the selection and safe application of high-speed train friction materials.

Synergistic Effects of Different Graphite on the Braking Performance of Cu-Matrix Friction Materials for High-Speed Trains Based on Pin–Disc Tests

Effects of Fe and graphite on friction and wear properties of brake friction materials for high-speed and heavy-duty vehicles

Effect of Type and Content of Iron Powder on the Formation of Oxidized Film and Tribological Properties of Cu-matrix Composites

Effects of Aluminosilicate Particles on Tribological Performance and Friction Mechanism of Cu-matrix Pads for High-Speed Trains

Effect of Iron Powder Type on Friction and Wear Properties of Copper-Based Friction Powder Metallurgy Material

Braking Performance of Copper-Based Friction Materials Reinforced by AlCoCrFeNi High-Entropy Alloy

Comparison of the Braking Behavior Among Cast Steel, Carbon/Carbon (C/C) and Carbon/Carbon-Silicon Carbide (C/C-SiC) Materials Mated with Copper-Based Composites

Effect of carbon fiber on the braking performance of copper-based brake pad under continuous high-energy braking conditions

Effect of Surface Modification on the Tribological Properties of Friction Blocks in High-Speed Train Brake Systems

Study on the Tribological Performance of Copper-Based Powder Metallurgical Friction Materials with Cu-Coated or Uncoated Graphite Particles as Lubricants

Comparison of Friction and Wear Behavior Between C/C, C/C-SiC and Metallic Composite Materials

Effect of Sintering Temperature on the Microstructure and Mechanical and Tribological Properties of Copper Matrix Composite for Brake Pads

On the tribological behaviors of Cu matrix composites with different Cu-coated graphite content

Tribological behavior and mechanism of h-BN modified copper metal matrix composites paired with C/C–SiC

Enhanced braking performance of copper metal matrix composites incorporating fine mosaic pitch coke when mated with 30CrMnVA and C/C-SiC

Wear Mechanism of Copper-based Powder Metallurgical Friction Materials with Different Graphite Content

A Study of the Microstructure and Tribological Properties of Copper-Based Cr@graphite Alloy Modified by Nano Cr3C2 and CrC

A Study of the Microstructure and Tribological Properties of Copper-Based Cr@graphite Alloy Modified by Nano Cr<sub>3</sub>C<sub>2</sub> and CrC

Research on the tribological properties of railroad brake shoes made of compacted graphite cast iron

Effect of Carbonaceous Components on Tribological Properties of Copper-Free NAO Friction Material

Influence of Braking Conditions on Tribological Performance of Copper-Based Powder Metallurgical Braking Material