Critical Rolling Process Parameters for Dynamic Recrystallization Behavior of AZ31 Magnesium Alloy Sheets.
Wenke Wang,Qing Miao,Xuemin Chen,Yang Yu,Wencong Zhang,Wenzhen Chen,Erde Wang
DOI: https://doi.org/10.3390/ma11102019
IF: 3.4
2018-01-01
Materials
Abstract:In this work, the influence of various rolling temperatures and thickness reductions on the dynamic recrystallization (DRX) behavior of AZ31 magnesium alloy sheets was investigated. Meanwhile, the texture variation controlled by DRX behavior was analyzed. Results suggested that, with the help of DRX behavior, reasonable matching of rolling temperature and thickness reduction could effectively refine the grain size and improve the microstructure homogeneity. Using the grain refinement and microstructure homogeneity as the reference, the critical rolling process parameters were 400 degrees C30%, 300 degrees C30%, and 250 degrees C40% in the present work. In terms of basal texture variation, the occurrence of twins produced the largest maximum texture intensity. However, for the sheets with DRX behavior, the maximum texture intensity decreased sharply, but would steadily increase with the growth of DRXed grain. Additionally, for DRXed grains, the <11-20>//RD (RD: rolling direction) grains would gradually annex the <10-10>//RD grains with the growth of DRXed grains, which finally made their texture component become the dominant texture state. However, when the deformation continued, the <10-10> in DRXed grains would rotate toward the RD again. Weighted by the fracture elongation of AZ31 magnesium alloy sheet, the critical thickness reductions were 30-40% under the rolling temperature of 400 degrees C.