Abstract:The effect of composition tuning on glass forming ability (GFA), mechanical properties and atomic structure in ZrxCo84−xAl16 bulk metallic glasses (BMGs) with x = 51–58 has been investigated by using copper-mold suction casting, nanoindentation, high-energy X-ray diffraction, extended X-ray absorption fine structure experiments and ab initio molecular dynamics simulations, respectively. It is found that GFA firstly increases then decreases with increasing Zr content, exhibiting a maximum diameter of 7 mm with the Zr content of 55 and 56, while an abrupt reduction of bending plasticity occurs as the Zr content drops below 55. Both experimental and theoretical results find that GFA is remarkably enhanced, due to the abnormal reduction in the fractions of the Co-centered ⟨0, 2, 8, 1⟩, ⟨0, 3, 6, 2⟩ and ⟨0, 3, 6, 3⟩ polyhedra, and the denser atomic packing of Zr atoms around center Co atom, as the Zr content increases from 51 to 56. Meanwhile, the simultaneously improved plasticity is associated with the increased Co-centered ⟨0, 3, 6, 0⟩, and Al-centered ⟨0, 2, 8, 1⟩ and ⟨0, 3, 6, 2⟩ polyhedra, which provide more fertile sites for the nucleation of shear transformations. Further Zr addition to 58 increases remarkably the fractions of Zr- and Al-centered ⟨0, 1, 10, 2⟩ and ⟨0, 3, 6, 4⟩ polyhedra, and causes looser atomic packing of Co atoms around center Zr atom, leading to the reduction in GFA. However, the plasticity is not enhanced further but remains nearly constant, which may be related to the deteriorated effect on plasticity of the decreased fractions of Zr-centered ⟨0, 1, 10, 5⟩ and Co-centered ⟨0, 3, 6, 0⟩ polyhedra, and the increased fractions of Zr-centered ⟨0, 1, 10, 3⟩ and ⟨0, 2, 8, 4⟩ and Co-centered ⟨0, 2, 8, 0⟩ polyhedra. Compositional tuning, with internal structure tuned to favor both GFA and plastic flow, offers new possibilities in developing ductile BMG materials.

Influence of Casting Temperature on the Castability and Glass-Forming Ability of Zr-based Bulk Metallic Glasses

Influence of the Melting Temperature on the Fabrication of A Ti-Cu-Zr-Ni-Sn Bulk Metallic Glass

Effect of Casting Temperature Control on Microstructure and Properties of Continuously Cast Zr-Based Bulk Metallic Glass Slabs

Determination of Forming Ability of High Pressure Die Casting for Zr-based Metallic Glass

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Enhancing strength and plasticity of Zr-based bulk metallic glasses by Zr partially substituted Fe and isothermal annealing

Effect of mold temperature on the solidification process and microstructure of Zr-based metallic glasses during casting

Fe–C micro-alloying effect on properties of Zr53Al11.6Ni11.7Cu23.7 bulk metallic glass

The temperature field characteristics and amorphous formation ability during the continuous casting process of Zr-based bulk metallic glass

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

73 Mm-Diameter Bulk Metallic Glass Rod By Copper Mould Casting

Numerical simulation and experimental verification of large-sized Zr-based bulk metallic glass ring-shaped parts in casting process

Ni-Free Zr-Based Bulk Metallic Glasses with Critical Diameter above 20 Mm

Glass forming ability and bending plasticity evolutions in Zr-Co-Al bulk metallic glasses and their structural origin

Glass Forming Ability and Corrosion Resistance of Zr-Cu-Ni-AlAg Bulk Metallic Glass

Synthesis of Bulk Zr48Cu36Al8Ag8 Metallic Glass by Hot Pressing of Amorphous Powders

High-temperature wear behavior of a Zr-based metallic glass

Ti Microalloying Effect on Corrosion Resistance and Thermal Stability of CuZr-based Bulk Metallic Glasses

The effect of impurities in zirconium on the formation and mechanical properties of Zr55Cu30Al10Ni5 metallic glass

Improving the Glass Forming Ability and Plasticity of Zrcunialti Metallic Glass by Substituting Zr with Sc

Effect of Ti addition on mechanical properties of Zr-based bulk metallic glasses