Abstract:In order to study the mechanical properties of seawater sea sand concrete and the durability damage law of seawater sea sand concrete under the action of seawater erosion, corresponding specimens were prepared and subjected to cube compressive strength, flexural strength, and dry-wet cycle tests by taking the volume dosage of glass fibers and polyvinyl alcohol fibers as variables. The test combined SEM scanning and EDS to analyze the microstructure of fiber-reinforced seawater sand concrete, and established a model based on the two-parameter Weibull probability distribution. The results show that the fiber has a significant effect on improving the mechanical properties and erosion resistance of seawater sand concrete. When the total volume content is 0.3% and the mixing ratio is 1:1, the improvement effect is the best. The maximum increase in cubic compressive strength was 24.2%; the maximum increase in flexural strength was 38.8%. After the specimens were subjected to wet and dry cycles for 360d, the maximum reduction in mass loss rate was 41.23%; the maximum reduction in strength loss rate was 27.55%. As observed from the microscopic images, the main disadvantage of SSC is that the salt crystallization and swelling matter produced by the erosion ions will weaken the bond between aggregate and mortar, resulting in defects in the interfacial transition zone (ITZ). Under the action of dry-wet cycles, the alternating dry-wet forces, the expansion pressure generated by expansive substances and the crystallization pressure generated by salt crystallization will change the microstructure, and therefore the damage of the specimen will deepen with the extension of erosion time. The microscopic images also show that the doping fibers can improve the internal integrity and compactness of the matrix, thus significantly improving the mechanical properties and durability of seawater sea sand concrete. In this test, a damage model was established based on the two-parameter Weibull distribution model, and the damage law between strength loss and dry-wet cycles was fitted, which provides a favorable basis to study the damage of seawater sea sand concrete under wet-dry cycling.

Deterioration Analysis of Seawater and Coral Sand Concrete in Simulated Marine Environment Based on CT Technique

A Strength Degradation Model of Saturated Soft Clay and Its Application in Caisson Breakwater

Degradation effect of seawater on the long-term dynamic behavior of artificially cemented sand

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Analysis of Early-Age Hydration Behavior and Micro-Mechanism of Coral Sand Cement Mortar

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Durability of MICP-reinforced Calcareous Sand in Marine Environments: Laboratory and Field Experimental Study

Deteriorated characteristics, elemental zonation, and phase changes in the surface of cemented soil exposed to marine environment

Drying–Wetting Correlation Analysis of Chloride Transport Behavior and Mechanism in Calcium Sulphoaluminate Cement Concrete

Study on mechanical properties and anti-erosion performance of fiber reinforced seawater sea sand concrete

Effect of ICCP on Bond Performance and Piezoresistive Effect of Carbon Fiber Bundles in Cementitious Matrix

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

The Effect of SCMs on the Resistance of Steam-cured Concrete to Chloride Attack in the Tidal Zone of Real Marine Environment

Modelling damage evolution of carbon fiber-reinforced epoxy polymer composites in seawater sea sand concrete environment

Durability of cementitious materials in seawater environment: A review on chemical interactions, hardened-state properties and environmental factors

Quantitative Characterization of Multiple Cracks and Permeability in Coral Sand Engineered Cementitious Composites Based on Micro-Computed Tomography

Capillary water absorption and free shrinkage characterization for seawater sea-sand concrete