Abstract:The incorporation of supplementary cementitious materials (SCMs) in concrete can improve the properties of concrete partially immersed in salt solution. However, the current partial immersion environment only considers the capillary action above the still water level, does not consider the capillary action above the fluctuating water level in dry-wet cycling environment. In this paper, a series of indoor exposure experiments were carried out to investigate the effects of incorporating polynary SCMs including fly ash (FA), ground granulated blast furnace slag (GGBFS) and silica fume (SF) on the sulfate resistance and chloride impermeability of concrete considering the capillary action above the fluctuating water level in dry-wet cycling environment. A total of 15 groups of concrete with different mix proportions (total 150 concrete specimens) were designed to study the effects of different replacement levels of polynary SCMs on concrete properties. The effects of incorporating polynary SCMs on the chloride impermeability of concrete above and in the fluctuating water level zone were investigated. The scanning electron microscope (SEM), x-ray diffraction (XRD) and mercury intrusion porosimetry (MIP) tests were used to analyze the microstructure of concrete. The results indicate that when concrete is incorporated with polynary SCMs and subjected to capillary action above the fluctuating water level, the compressive strength and chloride impermeability first increase and then decrease with the increase of FA content; the compressive strength and chloride impermeability decrease with the increase of GGBFS content; the compressive strength first increase and then decrease with the increase of SF content, and the chloride impermeability increase with that. The transport process of chloride in concrete above the fluctuating water level zone includes the longitudinal transport under capillary action and the transverse transport under concentration gradient action. The combined effects of both cause the higher chloride concentration in concrete above the fluctuating water level zone. Comprehensively considering the influence of different mix proportions on the sulfate resistance and chloride impermeability of concrete, it is determined that 20% FA + 5% SF is the optimal replacement level with the excellent performance considering the capillary action above the fluctuating water level in dry-wet cycling environment.

The Effect of SCMs on the Resistance of Steam-cured Concrete to Chloride Attack in the Tidal Zone of Real Marine Environment

Effects of Natural Seawater and Sea Sand on the Compressive Behaviour of Unconfined and Carbon Fibre-Reinforced Polymer-Confined Concrete

Effect of chloride penetration on CFRP sheet, CFRP‐concrete interface, and CFRP‐strengthened concrete beams

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone

Effect of steam curing on strength, durability and microstructure of concretes with and without mineral admixtures

Effects of incorporating polynary SCMs on sulfate resistance and chloride impermeability of concrete considering capillary action in dry-wet cycling environment

Research on the Resistance to Saline Soil Erosion of High-Volume Mineral Admixture Steam-Cured Concrete

Chloride transport resistance of alkali-activated concrete exposed to combined chloride, sulfate and carbonation environment

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Atmospheric chloride-induced corrosion of steel-reinforced concrete beam exposed to real marine-environment for 7 years

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Effect of Concrete Mixture Proportions on the Chloride Resistance

Drying–Wetting Correlation Analysis of Chloride Transport Behavior and Mechanism in Calcium Sulphoaluminate Cement Concrete

Investigation on chloride resistance of high-volume slag low-carbon cement-based materials with crystalline admixture under seawater

The Resistance of Novel Concrete Prepared by Gap-Graded Blended Cement under Chloride-Sulfate Attack

Influence of Steam Curing Method on the Performance of Concrete Containing a Large Portion of Mineral Admixtures