Abstract:Herein, triethanolamine additive is innovatively utilized to regulate the hydrothermal process of Sb2(S,Se)3 thin film. Ultimately, the longitudinal Se/(S+Se) ratio of Sb2(S,Se)3 thin film is well controlled. The enhanced vertical crystal orientations, the uniformed back surface gradient, the suppressed over band bending at PN junction and the passivated harmful VSe1 defects leading to an efficiency of 9.94% for Sb2(S,Se)3 solar cell. Antimony selenosulfide (Sb2(S,Se)3) solar cells have achieved an efficiency of over 10.0%. However, the uncontrollable hydrothermal process makes preparing high‐quality Sb2(S,Se)3 thin films a bottleneck for efficient Sb2(S,Se)3 solar cell. To address this problem, triethanolamine (TEA) additive is innovatively utilized to regulate the reaction kinetic process of Sb2(S,Se)3 thin films in this work. The results show that TEA chelator can realize the time‐domain control of the reaction process, optimizing the Se/(S+Se) elemental distribution of Sb2(S,Se)3 thin film and shrinking the bandgap offset of Sb2(S,Se)3 thin film. Meanwhile, the (021) and (061) crystal orientation of Sb2(S,Se)3 thin film are enhanced and the harmful VSe1 defects in Sb2(S,Se)3 solar cells are passivated. Interestingly, a uniform back surface gradient for Sb2(S,Se)3 thin film is formed to reduce the minority carrier recombination at the back contact, increase the photocurrent and decrease the diode current of Sb2(S,Se)3 solar cells. Finally, the Jsc and FF of Sb2(S,Se)3 solar cells are significantly improved by 8.6% and 5.5% respectively, and the open‐circuit voltage deficit of the device is reduced by 44 mV, which leads to an efficiency of 9.94% which is the highest values of Sb2(S,Se)3 solar cells by sodium selenosulfate system.

Low-Cost Antimony Selenosulfide with Tunable Bandgap for Highly Efficient Solar Cells

Pulsed laser deposition of antimony selenosulfide thin film for efficient solar cells

Fabricating High‐Efficiency Sb2(S,Se)3 Solar Cells by Novel Additive‐Assisted Longitudinal Component Engineering

Direct Hydrothermal Deposition of Antimony Triselenide Films for Efficient Planar Heterojunction Solar Cells

Hydrothermal deposition of antimony selenosulfide thin films enables solar cells with 10% efficiency

Research progress on tunable band gap antimony sulfoselenide thin films and solar cells

Temperature‐Gradient Solution Deposition Amends Unfavorable Band Structure of Sb2(S,Se)3 Film for Highly Efficient Solar Cells

HTL-Free Sb<sub>2</sub>(S, Se)<sub>3</sub> Solar Cells with an Optimal Detailed Balance Band Gap

Development of Antimony Sulfide–selenide Sb2(S, Se)3-based Solar Cells

Fabrication of Sb2S3 Thin Films by Magnetron Sputtering and Post-Sulfurization/selenization for Substrate Structured Solar Cells

Single-source Thermal Evaporation Converts Anion Controllable Sb 2 (s,se) 3 Film for Fabricating High-Efficiency Solar Cell

Suppressing Buried Interface Nonradiative Recombination Losses Toward High-Efficiency Antimony Triselenide Solar Cells

Suppressing Buried Interface Nonradiative Recombination Losses Towards High‐efficiency Antimony Triselenide Solar Cells

Confined‐Space Selenium‐Assisted Tellurization Posttreatment Strategy for Efficient Full‐Inorganic Sb2S3 Thin‐Film Solar Cells

Highly Efficient and Stable Planar Heterojunction Solar Cell Based on Sputtered and Post-Selenized Sb 2 Se 3 Thin Film

Selenium-Graded Sb-2(S1-xSex)(3) for Planar Heterojunction Solar Cell Delivering a Certified Power Conversion Efficiency of 5.71%

Bandgap grading via sputtering and post-selenization using SeS2 powder enabling Sb2(S,Se)3 solar cells with 7.1% efficiency

Chemical Etching Induced Surface Modification and Gentle Gradient Bandgap for Highly Efficient Sb2(S,Se)3 Solar Cell

Recent Achievements in Solution Processed Antimony Selenosulfide Solar Cells

Efficient Sb 2 (s,se) 3 Solar Modules Enabled by Hydrothermal Deposition

Bandgap Tunable CdS:O As Efficient Electron Buffer Layer for High-Performance Sb2Se3 Thin Film Solar Cells